  • IPEN-DOC 20195

    LIMA, SERGIO C.N. de ; SOARES, EDSON P. ; ANDREOLI, MARCO ; CHIBA, RUBENS ; SEO, EMILIA S.M. . Characterization of metallic zirconium sponge. Materials Science Forum, v. 805, p. 700-705, 2015. DOI: 10.4028/www.scientific.net/msf.805.700

    Palavras-Chave: zirconium alloys; porous materials; chlorination; microstructure; microhardness; fuel pellets; pwr type reactors; bwr type reactors; x-ray diffraction; fluorescence

  • IPEN-DOC 24312

    ICHIKAWA, RODRIGO U. ; YOSHITO, WALTER K. ; SAEKI, MARGARIDA J.; MARANHAO, WILLIAN C.A. ; GOULART, FATIMA ; MARTINEZ, LUIS G. . Characterization of Mn0.67Zn0.33Fe2O4 nanoparticles synthesized under different pH. Materials Science Forum, v. 899, p. 48-53, 2017. DOI: 10.4028/www.scientific.net/MSF.899.48

    Abstract: Nanostructured Mn-Zn ferrites were synthesized using co-precipitation in alkaline solution with different pH. The samples were characterized using X-ray diffraction (XRD), X-ray fluorescence (XRF), thermal analysis (TG-DTA), dynamic light scattering (DLS) and scanning electron microscopy (SEM) techniques. Monophasic nanoparticles were formed when synthesized with pH 10.5. This sample was heat-treated and its XRD data was refined by the Rietveld method. Mean crystallite sizes and microstrains were determined from X-ray line profile analysis using Single-Line and Warren-Averbach methods, which revealed a mean crystallite size of approximately 10 nm and negligible microstrains. Zn content was estimated using refined cell parameters, giving a value of 33 at %, in accordance with XRF result. TG-DTA revealed that the incorporation of α-Fe2O3 occurs around 1130 °C and 1200 °C with recrystallization of the Mn-Zn ferrite spinel phase. DLS showed that mean particle size increase with temperature up to 1159 nm at 800 °C. SEM analysis showed the samples agglomerate and present similar morphology with negligible size changing when calcined between 280 °C and 800 °C. However, the sample calcined at 1200 °C presents larger agglomerates due to the sintering process.

    Palavras-Chave: manganese compounds; zinc compounds; ferrites; nanoparticles; x-ray diffraction; thermal gravimetric analysis; differential thermal analysis; light scattering; scanning electron microscopy

  • IPEN-DOC 27404

    MARANHAO, W.C.A. ; ICHIKAWA, R.U. ; TURRILLAS, X.; YOSHITO, W.K. ; SAEKI, M.J.; ORLANDO, M.T.D.; MARTINEZ, L.G. . Characterization of nanostructured Mn-Zn ferrites synthesized by coprecipitation method using CTAB. Materials Science Forum, v. 1012, p. 207-211, 2020. DOI: 10.4028/www.scientific.net/MSF.1012.207

    Abstract: In this work it was investigated the influence of CTAB surfactant concentration on the synthesis of the compound Mn0.75Zn0.25Fe2O4 by the coprecipitation method. It was also compared the influence of hydrothermal treatment on the synthesized materials. The magnetic properties were characterized by AC susceptometry for the determination of the magnetic susceptibility and magnetic density energy. The phases, crystal structure and morphology of the nanoferrites were determined by Rietveld analysis of X-ray diffraction data. It was found the presence of two phases: Franklinite and Akaganeite and it was shown that the samples synthesized only by coprecipitation presented the tendency to increasing the crystallite sizes of the akaganeite phase and decreasing of crystallite sizes of the Franklinite phase as a function of CTAB concentration. The samples submitted to subsequent hydrothermal treatment presented a tendency to decreasing the crystallite sizes of both phases and increasing in Franklinite phase fraction, compared to the samples synthesized only by coprecipitation, suggesting that the hydrothermal treatment was effective in obtaining nanostructured materials of smaller particles.

    Palavras-Chave: ferrites; manganese; zinc; nanostructures; manganese carbides; zinc oxides; coprecipitation; hydrothermal synthesis; x-ray diffraction; calculation methods

  • IPEN-DOC 15663

    SANTORO, T.A.B.; OLIVEIRA NETO, A. ; CHIBA, R.; SEO, E.S.M. ; FRANCO, E.G.. Characterization of proton exchange membrane fuel cell cathode catalysts prepared by alcohol-reduction process. Materials Science Forum, v. 660-661, n. 7, p. 94-99, 2010.

    Palavras-Chave: proton exchange membrane fuel cells; cathodes; platinum; lanthanum oxides; carbon; rare earths; hydrogen; electrocatalysts

  • IPEN-DOC 09708

    SALIBA SILVA, A.M. ; MELO, H.G.; BAKER, M.A.; BROWN, A.M.; COSTA, I. . Characterization of sintered NdFeB magnets after phosphating in alkaline and acid environments. Materials Science Forum, v. 416/418, p. 54-59, 2003.

    Palavras-Chave: permanent magnets; iron alloys; neodymium alloys; boron alloys; corrosion protection; phosphates; corrosion resistance; protective coatings; corrosion; impedance; spectroscopy

  • IPEN-DOC 13727

    AGUIAR, AMANDA A.; USSUI, VALTER ; RIBEIRO, CHRISTIANE; SCAPIN, MARCOS A. ; RICCI, DOLORES R. ; LIMA, NELSON B. de . Characterization of the apatite formation on the surfaces of zirconia and alumina ceramics in body environments. Materials Science Forum, v. 591-593, p. 697-702, 2008.

    Palavras-Chave: biological materials; apatites; nucleation; zirconium oxides; aluminium oxides; body fluids; crystallography; crystal structure

  • IPEN-DOC 09680

    MOURA, S.C. ; LIMA, N.B. ; LIMA, L.M.F.G. ; SASSINE, A.; VEGA BUSTILLOS, J.O.W. . Characterization of the stoichiometric ratio O/U in UOsub(2) samples by gravimetric and voltametric methods. Materials Science Forum, v. 416/418, p. 737-742, 2003.

    Palavras-Chave: uranium dioxide; nuclear fuels; stoichiometry; oxygen; uranium; concentration ratio; gravimetric analysis; voltametry; x-ray diffraction

  • IPEN-DOC 20115

    MUCCILLO, E.N.S. ; GONCALVES, M.D.; GROSSO, R.L. ; MUCCILLO, R. . Characterization of yttrium-doped barium zirconate nanocrystalline powder prepared by spray pyrolysis. Materials Science Forum, v. 798-799, p. 407-412, 2014.

    Palavras-Chave: yttrium; doped materials; barium; zirconates; nanostructures; crystals; powders; sprays; pyrolysis; microstructure

  • IPEN-DOC 09700

    LEAL NETO, R.M. ; ROCHA, C.J. ; AMBROZIO FILHO, F. . Combustion synthesis of high-energy ball-milled Nb+3Al powder mixtures. Materials Science Forum, v. 416/418, p. 156-161, 2003.

    Palavras-Chave: intermetallic compounds; combustion; synthesis; niobium; aluminium; powders; milling; density; microstructure; mechanical properties; alloys

  • IPEN-DOC 11215

    BURACOVAS, F.; GONCALVES, V.S.; ROCHA, C.J. ; LEAL NETO, R.M. . Combustion synthesis of mechanically-activated Nb-Al mixtures. Materials Science Forum, v. 498/499, p. 152-157, 2005.

    Palavras-Chave: cutting tools; steels; combustion; synthesis; iron base alloys; grain size; heat treatments; mechanical properties; alloys

  • IPEN-DOC 13729

    YOSHITO, W.K. ; SCAPIN, M.A. ; USSUI, V. ; LAZAR, D.R.R. ; PASCHOAL, J.O.A. . Combustion synthesis of NiO/YSZ composite. Materials Science Forum, v. 591-593, p. 777-783, 2008.

    Palavras-Chave: nickel oxides; yttrium oxides; powders; synthesis; combustion; electrodes; solid oxide fuel cells

  • IPEN-DOC 06946

    LEAL NETO, R.M. ; FERREIRA, P.I. . Combustion synthesis reactions in the Nb-Ni-Al system. Materials Science Forum, v. 299/300, p. 271-276, 1999.

    Palavras-Chave: combustion; synthesis; niobium alloys; nickel alloys; aluminium alloys; scanning electron microscopy; calorimetry

  • IPEN-DOC 06954

    PANELLI, R.; AMBROZIO FILHO, F. . Compaction of AISI M2+ 10 percent vol. NbC processed by high energy mill. Materials Science Forum, v. 299/300, p. 463-469, 1999.

    Palavras-Chave: composite materials; powders; milling; compacting; particle size; mechanical properties; alloys

  • IPEN-DOC 16526

    REIS, D.A.P.; MOURA NETO, C.; SILVA, M.M.; UEDA, M.; OLIVEIRA, V.S.; COUTO, A.A. . Comparation between PIII superficial treatment and ceramic coating in creep test of Ti6Al-4V alloy. Materials Science Forum, v. 660-661, p. 225-228, 2010.

    Palavras-Chave: aluminium alloys; titanium alloys; vanadium alloys; creep; plasma; spray coating

  • IPEN-DOC 16527

    REIS, A.G.; REIS, D.A.P.; MOURA NETO, C.; ONÕRO, J.; OLIVEIRA, H.S.; COUTO, A.A. . Comparation between pulsed Nd:YAG laser superficial treatment and ceramic coating in creep test of Ti6Al-4V alloy. Materials Science Forum, v. 660-661, p. 229-234, 2010.

    Palavras-Chave: titanium alloys; creep; plasma; spray coating; laser radiation; pulsed irradiation

  • IPEN-DOC 14468

    PERIGO, E.A.; SOARES, E.P.; TAKIISHI, H. ; MOTTA, C.C.; FARIA, R.N. . A comparative study between low and high-energy milling processes for the production of HD PrFeCoBNb sintered materials. Materials Science Forum, v. 591-593, p. 114-119, 2008.

    Palavras-Chave: hydrogen; permanent magnets; sintered materials; magnets; comparative evaluations; milling; magnetic properties

  • IPEN-DOC 15911

    MARQUES, R.A.; SALIBA SILVA, A.M. ; ROGERO, S.O. ; MONTEMOR, M.F.; COSTA, I. . A comparative study of the corrosion resistance of stainless steels obtained by powder metallurgy techniques for application in dental prosthesis. Materials Science Forum, v. 660-661, p. 617-622, 2010.

    Palavras-Chave: stainless steels; ferromagnetic materials; corrosion resistance; powder metallurgy; prostheses; teeth; simulation; pitting corrosion

  • IPEN-DOC 24866

    MACHADO, GLAUSON A.F. ; ROCHA, ROSA M.; BRESSIANI, ANA H.A. . Composites obtained from alumina and polymer derived ceramic. Materials Science Forum, v. 912, p. 141-146, 2018. DOI: 10.4028/www.scientific.net/MSF.912.141

    Abstract: Alumina-mullite composites with low shrinkage can be made by reaction bond using mixtures of alumina, aluminum and silicon carbide. In this work, an alternative route is used to produce alumina composites with low shrinkage. Here alumina samples containing additions of 10 and 20 wt% of a preceramic polymer were warm-pressed and treated in the range of 900 -1500°C to produce alumina based composites. The obtained composites were analyzed by linear shrinkage and compared to pure alumina samples sintered at the same temperature range. It were also evaluated the density variation and crystalline phases formed during heat treatment of alumina composites. Results showed that alumina-silicon oxycarbide and alumina-mullite composites were obtained with lower shrinkage than pure alumina samples.

    Palavras-Chave: composite materials; silicon carbides; polymers; mullite; aluminium oxides; ceramics; pyrolysis

  • IPEN-DOC 06948

    MELO, F.C.L.; SILVA, C.R.M.; BRESSIANI, A.H.A. ; BRESSIANI, J.C. . Composition effects on the microstructure and mechanical properties of sintered boron carbide. Materials Science Forum, v. 299/300, p. 13-18, 1999.

    Palavras-Chave: boron carbides; sintering; microstructure; mechanical properties

  • IPEN-DOC 11218

    MUCSI, C.S. ; FARIA, R.N. ; GALEGO, E. ; ROSSI, J.L. . Consolidation of compacted zircaloy chips via vacum are melting - analysis of the electric arc. Materials Science Forum, v. 498/499, p. 258-263, 2005.

    Palavras-Chave: electric arcs; zircaloy; var control systems; fuel-cladding interactions; compacting; phase transformations; arc furnaces; melting

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.