  • IPEN-DOC 29905

    RIBEIRO, GLEICY de L.X. ; CASTRO, RENATO S. de; SANTOS, ROGERIO G. dos; BUGARIN, ALINE de F.S. ; TERADA, MAYSA; BATALHA, GILMAR F.; COUTO, ANTONIO . Characterization of Ti6Al4V alloy produced by laser-powder bed fusion and surface modification using nanosecond laser. Materials Research, v. 26, Suppl.1, p. 1-5, 2023. DOI: 10.1590/1980-5373-MR-2022-0544

    Abstract: Ti alloys are widely used in severe corrosion environments where corrosion resistance is required, as biomedical industry. Additive manufacturing produces customized and complexes products. Laser texturing is a process of structuring surfaces using laser pulses, that allows the creation of periodic patterns on the surfaces of materials, to modify them, functionally and/or aesthetically, in a precise and direct way, allowing parameterization, versatility and repeatability. Consequently, bringing together metallic additive manufacturing with laser texturing process could be an alternative to obtain parts with functional hydrophilic surfaces, which improves osteointegration and reduces bacteria adhesion. Thus, the aim of this work is to characterize and evaluate the influence of LASER parameters in as-built additive manufactured potential biomedical components. Ti6Al4V specimens were produced by L-PBF, using Ytterbium LASER with maximum power of 500 W, varying the laser power from 61 W to 244 W. The samples were characterized by SEM, Microhardness, and wettability. After that, some specimens were Laser textured using an Ytterbium optical fiber laser, and then evaluated by SEM, wettability, and 3D roughness. It was possible to observe that the surface of all studied samples was flattened after Laser texturing in comparison with as-built condition, due to the melting of the powder particles.

    Como referenciar este item
    Icon

  • IPEN-DOC 23347

    BUGARIN, ALINE de F.S. . Estudo da resistência à corrosão das ligas de alumínio 2024-T3 e 7475-T651 soldadas por fricção e mistura (FSW) / Study of the corrosion resistance of aluminium alloys 2024-T3 and 7475-T651 welded by friction stir welding (FSW) . 2017. Dissertação (Mestrado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 119 p. Orientador: Isolda Costa. DOI: 10.11606/D.85.2017.tde-26102017-141238

    Abstract: O processo de soldagem por fricção e mistura (FSW) tem despertado grande interesse nos últimos anos e tornou-se uma alternativa para unir materiais de baixa soldabilidade, como as ligas de alumínio das séries 2XXX e 7XXX, as quais são empregadas na estrutura das aeronaves, por possuírem elevada relação resistência/peso. O processo FSW, todavia, causa mudanças microestruturais nos materiais soldados, particularmente na zona misturada (ZM) e nas zonas termicamente (ZTA) ou termomecanicamente (ZTMA) afetadas. Estas mudanças geralmente interferem no desempenho frente à corrosão das ligas soldadas. No presente estudo, a resistência à corrosão das ligas de alumínio 2024-T3 e 7475-T761, unidas pelo processo FSW foi investigada em solução 10 mM de NaCl. Ensaios de visualização em gel ágar-ágar e de imersão associados a técnicas microscópicas foram realizados para investigar o efeito do acoplamento galvânico na corrosão das diferentes regiões da junta soldada. Os resultados do ensaio de visualização em gel mostraram que, quando acopladas, a liga 2024 atua como cátodo e a 7475 como ânodo. Os ensaios de imersão revelaram acoplamento galvânico entre as ligas na zona misturada (ZM). A região mais afetada pela corrosão foi a ZTMA da liga 7475, com corrosão intergranular desde as primeiras horas de imersão. A influência do processo de soldagem na resistência à corrosão das duas ligas de alumínio foi investigada por ensaios eletroquímicos. Os ensaios eletroquímicos adotados foram medidas de potencial de circuito aberto (PCA) em função do tempo de exposição ao meio corrosivo, espectroscopia de impedância eletroquímica (EIE) e curvas de polarização potenciodinâmica. Os ensaios de polarização mostraram elevada atividade eletroquímica na zona de mistura indicada pelos altos valores de densidade de corrente em comparação com as demais zonas testadas. Os resultados de EIE globais mostraram que nas primeiras horas de exposição ao eletrólito o processo de corrosão foi predominantemente controlado pela liga 7475; todavia, com o tempo de exposição ao eletrólito, a corrosão passou a ser controlada pela liga 2024.

    Palavras-Chave: corrosion resistant alloys; pitting corrosion; friction factor; friction welding; solid state physics; electrochemical corrosion; mechanical impedance; bimetals; materials testing; microstructure; electric impedance; spectroscopy

    Como referenciar este item
    Icon

  • IPEN-DOC 27430

    ARAUJO, JOAO V. de S. ; MILAGRE, MARIANA X. ; FERREIRA, RAPHAEL O.; MACHADO, CARULINE de S.C. ; BUGARIN, ALINE de F.S. ; MACHADO, IZABEL F.; COSTA, ISOLDA . Exfoliation and intergranular corrosion resistance of the 2198 Al–Cu–Li alloy with different thermomechanical treatments. Materials and Corrosion - Werkstoffe und Korrosion, v. 71, n. 12, p. 1957-1970, 2020. DOI: 10.1002/maco.202011839

    Abstract: In this study, the resistance to exfoliation and intergranular corrosion (IGC) of the 2198 Al–Cu–Li alloy submitted to different thermomechanical treatments (T3, T8, and T851) was investigated. The tests were carried out following the standard practices, ASTM G34‐18 and ASTM G110‐15, respectively. All the tested alloys showed susceptibility to exfoliation and some alloys showed susceptibility to IGC, but the artificially aged alloys presented a higher tendency to exfoliation. The extensive hydrogen evolution reaction (HER) was observed on the surfaces of artificially aged alloys when immersed in the EXCO solution. The HER resulted in an increase in solution pH with the time of immersion. Also, the weight losses related to the artificially aged alloys were higher than that of the naturally aged ones. The T8 treatment was the only condition that resulted in susceptibility to both, intergranular and transgranular corrosion, whereas the T851 treatment did not show IGC susceptibility, only transgranular corrosion. Finally, the 2198‐T3 condition showed the highest corrosion resistance among the thermomechanical treatments tested. The results of the 2198 alloy subjected to various treatments were compared with that of the 2024‐T3 alloy. This last alloy showed higher resistance to exfoliation and IGC as compared with the 2198 alloy.

    Palavras-Chave: corrosion; corrosion resistance; intergranular corrosion; thermomechanical treatments; aluminium alloys; copper alloys; lithium alloys; optical systems; emission spectroscopy; plasma; friction welding

    Como referenciar este item
    Icon

  • IPEN-DOC 30167

    BUGARIN, ALINE de F.S. ; RIBEIRO, GLEICY de L.X.; CASTRO, RENATO S. de; QUEIROZ, FERNANDA M.; SANTOS, ROGERIO G. dos; TERADA, MAYSA; COSTA, ISOLDA . Influence of texturing parameters on surface modification of UNS S32101 duplex steel. In: BRAZIL MRS MEETING, 21st, October 1-5, 2023, Maceió, AL. Abstract... São Carlos, SP: Aptor Software, 2023. p. 1373-1373.

    Abstract: The application of laser texturing aims to modify the surface without changing its chemical composition. These alterations can be evaluated through mechanical, physical or chemical tests. Texturing can be applied to improve efficiency in industrial processes, such as the flowability of materials, by applying laser texturing to the internal surfaces of components. This work aims to evaluate the influence of texturing parameters in the flow process of industrial batchers. UNS S32101 lean duplex stainless steel (LDSS) samples were used for the tests. For laser texturing of the surfaces, laser of Yb was used, with a wavelength of 1064 nm (infrared), using the scanning speed of 140 mm/s and pulse duration of 150 ns. Two sets of textured samples were produced: with a frequency of 50 kHz and 2 kHz. In both frequencys, the power(%) was set at 100, 60 and 20. The effect of texturing was analyzed through microstructural characterization with tests of contact angle, roughness and scanning electron microscopy.

    Como referenciar este item
    Icon

  • IPEN-DOC 30168

    QUEIROZ, FERNANDA M.; RIBEIRO, GLEICY de L.X.; CASTRO, RENATO S. de; SANTOS, ROGERIO G. dos; BUGARIN, ALINE de F.S. ; TERADA, MAYSA. Influence of the additive manufacturing parameters on the Ti6Al4V microstructure. In: BRAZIL MRS MEETING, 21st, October 1-5, 2023, Maceió, AL. Abstract... São Carlos, SP: Aptor Software, 2023. p. 1374-1374.

    Abstract: The 3D printing on an industrial scale describe the one more advanced techniques. In the manufacturing process technology the model is created by successively layering material from a digital 3D model. The 3D manufacturing process allows obtaining complex geometry, weight reduction, and customized components. A careful microstructure characterization of the produced components is necessary, since the parameters influence in surface roughness, microhardness and corrosion resistance. Samples of Ti6Al4V built with the same laser speed, hatch distance and layer thickness but different laser power were analyzed. The variation in laser power influenced the roughness and corrosion resistance of the samples.

    Como referenciar este item
    Icon

  • IPEN-DOC 29855

    QUEIROZ, FERNANDA M. ; BUGARIN, ALINE de F.S. ; AYUSSO, VICTOR H. ; TERADA, MAYSA; COSTA, ISOLDA . Investigation on the Effect of a Chromium-Free Sealing Treatment for the Corrosion Resistance of AA2198-T851 after Tartaric Sulphuric Anodizing (TSA). Corrosion and Materials Degradation, v. 4, n. 2, p. 331-344, 2023. DOI: 10.3390/cmd4020017

    Abstract: The AA 2198-T851 is a third-generation Al-Li alloy developed for use in the aircraft industry. Al-Li alloys are susceptible to localized corrosion due to their complex microstructure resulting from the used thermomechanical treatment. In order to prevent localized corrosion, these alloys are usually protected by anodizing in order to avoid a corrosive environment. Subsequently, for anodizing, a sealing treatment is usually performed for parts. Some sealing treatments use hexavalent-chromiumion-containing solutions. In this investigation, a chromium-free sealing treatment in a solution with cerium ions has been carried out, and the effect on the corrosion resistance of the AA2198-T851 alloy was investigated. Hydrothermally sealed or unsealed samples were also tested for corrosion resistance for comparison reasons. The corrosion resistance of the anodized aluminum alloy, either hydrothermally sealed or in a cerium-ion-containing solution, was evaluated in a sodium chloride solution by electrochemical impedance spectroscopy as a function of immersion time. The samples sealed in a cerium-containing solution increased their corrosion resistance when compared to the hydrothermally sealed. The effectiveness of the sealing process with cerium that was observed in the electrochemical tests indicated that after the corrosive attack of the barrier layer, there was a “sealing” process of the sample surface.

    Palavras-Chave: corrosion resistance; tartaric acid; sulfuric acid; anodization; cerium ions

    Como referenciar este item
    Icon

  • IPEN-DOC 29189

    BUGARIN, ALINE de F.S. ; VIVEIROS, BARBARA V.G. de ; TERADA, MAYSA; SILVA, LEANDRO S. da; GUILHERME, LUIS H.; NEVES, MAURICIO D.M. das ; COSTA, ISOLDA . Study of the corrosion resistance of duplex and lean duplex steels welded by the gas tungsten arc welding double fusion (GTAW-DF) applied in the construction of tanks. In: BRAZIL MRS MEETING, 20th, September 25-29, 2022, Foz do Iguaçu, PR. Abstract... São Carlos, SP: Aptor Software, 2022.

    Abstract: Duplex stainless steels has great technological importance due to the combination of high mechanical strength, high toughness and excellent corrosion resistance. New methods of joining these materials have been investigated and updated, with better cost-benefit. In this work, joints welded by the TIG process with root pass by the double-fusion method (GTAW-DF), typically applied in the construction of tanks for the citrus juice and biotechnology industry were investigated. The welding process of steels changes in its microstructures forming of deleterious precipitates which decrease the corrosion resistance. Thus, the aim of this work was to evaluate and compare the corrosion resistance after welding by the GTAW-DF process of similar joints of lean duplex 2101 steel and dissimilar joints of 2205 and 2304 steels, duplex and lean duplex respectively, both used in the citrus juice industry. Samples were made using optimized welding parameters under corrosion resistance criteria. Microstructural characterization was performed by metallographic etching and observation by optical microscopy (OM) and by scanning electron microscopy (SEM). Mechanical properties were evaluated by microhardness test. Corrosion resistance was evaluated by electrochemical tests by the double loop electrochemical potentiokinetic reactivation test (DL-EPR) and potentiodynamic polarization test. The results showed that the welding process caused microstructural changes in the materials, and that after welding the most susceptible regions to corrosion were in the fusion line and in the thermally affected zone. When analyzing the two welding conditions, it was observed that the welded samples with higher heat input showed lower tendencies to intergranular corrosion.

    Como referenciar este item
    Icon

  • IPEN-DOC 30166

    BUGARIN, ALINE de F.S. ; VIVEIROS, BARBARA V.G. de ; TERADA, MAYSA; GUILHERME, LUIS H.; NEVES, MAURICIO D.M. das ; COSTA, ISOLDA . Syringe cell method to study the corrosion resistance of the UNS S32101 lean duplex stainless steel welded by the gas tungsten arc welding double fusion (GTAW-DF). In: BRAZIL MRS MEETING, 21st, October 1-5, 2023, Maceió, AL. Abstract... São Carlos, SP: Aptor Software, 2023. p. 1178-1178.

    Abstract: This work aims to investigate the corrosion performance of the UNS S32101 lean duplex stainless steel (LDSS) welded by the gas tungsten arc welding double fusion (GTAW-DF). In the study, six welded samples were manufactured with different welding parameters. A Syringe cell was used to characterize the electrochemical behavior of the different welded zones by potentiodynamic polarization tests in NaCl 3,5 % (w.t.) and in a solution of citric acid with addiction of NaCl to simulate the food industry. The results showed that the welding parameters tested significantly affected the corrosion resistance of the LDSS UNS S32101. Besides, a correlation was stablished between microstructure and electrochemical behavior of fusion line (FL), heat affected zone (HAZ) and fusion zone (FZ).

    Como referenciar este item
    Icon

  • IPEN-DOC 25934

    ARAUJO, JOAO V. de S. ; BUGARIN, ALINE de F.S. ; DONATUS, UYIME ; MACHADO, CARULINE de S.C. ; QUEIROZ, FERNANDA M. ; TERADA, MAYSA ; ASTARITA, ANTONELLO; COSTA, ISOLDA . Thermomechanical treatment and corrosion resistance correlation in the AA2198 Al–Cu–Li alloy. Corrosion Engineering, Science and Technology, v. 54, n. 7, p. 575-586, 2019. DOI: 10.1080/1478422X.2019.1637077

    Abstract: The influence of T3, T8 and T851 thermomechanical treatments on the microstructure and corrosion resistance of the AA2198 was investigated. Differential scanning calorimetry and scanning electron microscopy were used for microstructural characterisation, whereas electrochemical methods were employed to analyse the corrosion behaviour of the alloy. The morphology and composition of constituent particles were similar for the T3 and T8 thermomechanical treatments but varied in the T851. There was an inverse relation between T1 phase density and corrosion resistance. The T3 treatment with the highest corrosion resistance was the one with the lowest density of T1 phase. The mechanisms of corrosion varied with the thermomechanical treatments.

    Palavras-Chave: thermomechanical treatments; aluminium alloys; lithium alloys; microstructure; copper alloys; corrosion resistant alloys; heat treatments

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.