Navegação por Revista "Defect and Diffusion Forum"

Classificar por: Ordenar: Resultados:

  • IPEN-DOC 23960

    REIS, ADRIANO G. dos ; REIS, DANIELI A.P.; ABDALLA, ANTONIO J.; COUTO, ANTONIO A. ; OTUBO, JORGE. An in situ high-temperature x-ray diffraction study of phase transformations in maraging 300 steel. Defect and Diffusion Forum, v. 371, p. 73-77, 2017. DOI: 10.4028/www.scientific.net/DDF.371.73

    Abstract: An in situ high-temperature X-ray diffraction (HTXRD) study in maraging 300 steel was carried out to study the martensite to austenite transformation and effect of time of exposure in the austenite reversion below austenite start temperature. Solution annealed materials were subjected to controlled heating-holding cycles. The first sample was heated at a rate of 10 ºC/min from room temperature to 800 ºC, showing that the microstructure is completely martensitic (α’110) until 600 ºC. From 650 ºC until 800 ºC, the microstructure is gradually changing from martensitic to austenitic, showed by the increasing peaks of γ111 and reducing peaks of α’110. At 800 ºC the microstructure is completely austenitic (γ111). Another sample was heated at 10 ºC/min from room temperature to 600 ºC and held for 4 hours. At 600 ºC, at 0 h time of exposure, only a martensitic peak was observed. An austenite peak can be observed after some time of exposure at this temperature. The volume fraction of austenite increased with increasing time of exposure at 600 ºC, reaching 50/50 volume fraction after 4 hours of exposure. XRD diffraction patterns for the same sample that was held for 4 hours at 600 ºC and then cooled down in air to room temperature showed the same intensity of austenite and martensitic peaks found in situ at 600 ºC for 4 hours (retained austenite), with the volume fraction of 50/50 of austenite and martensite phases. The HTXRD technique can be used to identify and quantify martensite to austenite transformation and austenite retention.

    Palavras-Chave: x-ray diffraction; maraging steels; temperature range 1000-4000 k; phase transformations; austenite

    Como referenciar este item
    Icon

  • IPEN-DOC 28600

    MONTEIRO, P.S.P.; SANTOS, G.A. dos; NAKAMOTO, F.Y. ; NASCIMENTO, M.S. ; TERAM, R.; SANTOS, V.T. dos; SILVA, M.R. da; COUTO, A.A. ; MACHADO, I.F.; BRANDI, S.D.. Analysis of the influence of continuous-drive friction welding on the microstructure and mechanical properties of the UNS C64200 bronze-aluminum-silicon alloy. Defect and Diffusion Forum, v. 412, p. 185-195, 2021. DOI: 10.4028/www.scientific.net/DDF.412.185

    Abstract: Friction welding (FRW) is an important commercial solid-state welding process in which coalescence is achieved by frictional heat combined with pressure. The objective of this work is to analyze the microstructure and the mechanical behavior of the copper alloy UNS C64200 – bronze-aluminum- silicon, as well as to raise the ideal welding parameters so that there is adequate weldability after process of continuous-drive friction welding. Regarding the analysis of the microstructure, scanning electron microscopy was used to characterize phases. The mechanical properties were evaluated by means of a hardness test of the center of the welded joint, traversing the entire extent of the thermally affected zone. Results show that the UNS C64200 alloy, when subjected to conventional friction welding, behaves satisfactorily in terms of weldability, without the appearance of cracks or defects arising from the temperature characteristic of this process, as well as good hardness with values above the minimum established in norm and higher than the base material.

    Palavras-Chave: microstructure; hardness; tin alloys; aluminium alloys; silicon alloys; friction welding

    Como referenciar este item
    Icon

  • IPEN-DOC 18364

    SUGAHARA, T.; MARTINOLLI, K.; REIS, D.A.P.; MOURA NETO, C.; COUTO, A.A. ; PIORINO NETO, F.; BARBOZA, M.J.R.. Creep behavior of the Inconel 718 superalloy. Defect and Diffusion Forum, v. 326-328, p. 509-514, 2012.

    Palavras-Chave: inconel 718; heat resisting alloys; creep; microstructure; scanning electron microscopy

    Como referenciar este item
    Icon

  • IPEN-DOC 18671

    BRIGUENTE, L.A.N.S.; COUTO, A.A. ; GUIMARAES, N.M.; REIS, D.A.P.; MOURA NETO, C.; BARBOZA, M.J.R.. Determination of creep parameters of Ti-6Al-4V with biomodal and equiaxed microstructure. Defect and Diffusion Forum, v. 326-328, p. 520-524, 2012.

    Palavras-Chave: aluminium alloys; titanium base alloys; vanadium alloys; creep; microstructure; heat treatments

    Como referenciar este item
    Icon

  • IPEN-DOC 18667

    REIS, D.A.P.; COUTO, A.A. ; DOMINGUES JUNIOR, N.I.; HIRSCHMANN, A.C.O.; ZEPKA, S.; MOURA NETO, C.. Effect of artificial aging on the mechanical properties of an aerospace aluminium alloy 2024. Defect and Diffusion Forum, v. 326-328, p. 193-198, 2012.

    Palavras-Chave: aerospace industry; aluminium alloys; aging; mechanical properties; precipitation

    Como referenciar este item
    Icon

  • IPEN-DOC 18680

    MARTINOLLI, KARINA; SUGAHARA, TARCILA; REIS, DANIELI; MOURA NETO, CARLOS de; HIRSCHMANN, ANA C.; COUTO, ANTONIO A. . Evaluation of inconel 718 creep behavior. Defect and Diffusion Forum, v. 326-328, p. 525-529, 2012.

    Palavras-Chave: inconel 718; creep; temperature range 0400-1000 k; heat resisting alloys

    Como referenciar este item
    Icon

  • IPEN-DOC 18668

    COUTO, A.A. ; ANDRADE, A.H.P. ; REIS, D.A.P.; ZEPKA, S.. Failure analysis of an automotive component (Cardan Yoke) by scanning electron microscopy. Defect and Diffusion Forum, v. 326-328, p. 187-192, 2012.

    Palavras-Chave: automotive accessories; failures; fractures; fatigue; mechanical properties; scanning electron microscopy

    Como referenciar este item
    Icon

  • IPEN-DOC 26905

    GALIZONI, BRENO B.; COUTO, ANTONIO A. ; REIS, DANIELI A.P.. Heat treatments effects on nickeI-based superalloy Inconel 713C. Defect and Diffusion Forum, v. 390, p. 32-40, 2019. DOI: 10.4028/www.scientific.net/DDF.390.32

    Abstract: The purpose of this work is to study the effect of heat treatments on the microstructure of the nickel-based superalloy Inconel 713C. Three different conditions were studied and the results compared: (1) as cast; (2) solution treatment (1,179°C/2h) and (3) stabilizing treatment (1,179°C/2h plus 926°C/16h). Inconel 713C is normally used in the as-cast condition, an improvement in the 980°C stress-rupture life is often obtained by a solution heat treatment. However, the material in this condition tested under high stress at 730°C shows a marked decreased in rupture life and ductility [1]. The mechanical resistance in creep increases in Inconel 713C by precipitation hardening phase, such γ’ (Ni3Al) formed during the heat treatments [2]. The characterization techniques used was: chemical analysis, hardness test, X-ray diffraction, optical microscope and scanning electron microscopy (SEM), EDS analyzes and thermocalculation. The heat treatments modified the dendritic structure, reducing the acicularity. The SEM and EDS analysis illustrated the γ, γ’ and carbides. The matrix phase (γ), has in its constitution the precipitation of the γ’ phase, in a cubic form, and in some regions, veins of carbides were modified with the heat treatments.

    Palavras-Chave: heat treatments; alloys; inconel 713c; microstructure; nickel base alloys; chemical analysis; mechanical properties

    Como referenciar este item
    Icon

  • IPEN-DOC 17249

    CARBONARI, ARTUR W. ; MESTNIK FILHO, JOSE ; SAXENA, RAJENDRA N. . Impurities in magnetic materials studied by PAC spectroscopy. Defect and Diffusion Forum, v. 311, p. 39-61, 2011. DOI: 10.4028/www.scientific.net/ddf.311.39

    Palavras-Chave: magnetic fields; hyperfine structure; perturbed angular correlation; spectroscopy; magnetic moments; magnetic materials

    Como referenciar este item
    Icon

  • IPEN-DOC 23991

    MIRANDA, FABIO; RODRIGUES, DANIEL; NAKAMOTO, FRANCISCO Y.; FRAJUCA, CARLOS; SANTOS, GIVANILDO A. dos; COUTO, ANTONIO A. . Microstructural evolution of composite 8 WC-(Co, Ni): effect of the addition of SiC. Defect and Diffusion Forum, v. 371, p. 78-85, 2016. DOI: 10.4028/www.scientific.net/DDF.371.78

    Abstract: Tungsten carbide (WC) based cemented carbides, also called hardmetals, are a family of composite materials consisting of carbide ceramic particles embedded in a metallic binder. They are classified as metal matrix composites (MMCs) because the metallic binder is the matrix that holds the bulk material together [1]. WC based composites are used in applications where a good combination of hardness and toughness are necessary [2]. It is usual to add more components to tailor the microstructure of the WC-(Co, Ni) system. The hardness for the cemented carbides based on nickel, increases significantly because of the addition of reinforcements like SiC nano-whisker [3]. In this work, the SiC was considered as an additional component for the composite WC-8(Co, Ni). Four mixtures were prepared with SiC contents ranging from 0 to 3.0 wt%. These mixtures were pressed (200 MPa) and green samples with 25.2 mm of diameter and 40 g were produced. Sintering was carried out in Sinter-HIP furnace (20 bar). Two sintering temperatures were investigated, i.e. 1380 and 1420ºC, and the sintering time considered was 60 minutes. The relative density, hardness, linear and volumetric shrinkage were determined. Microstructural evaluation was investigated by optical microscopy and scanning electron microscopy (SEM-FEG). The results showed that the addition of SiC promoted higher densification and grain size growth. The hardness was higher for samples with SiC, so solid solution hardening of the binder was more effective than WC grain size growth.

    Palavras-Chave: composite materials; sintering; tungsten carbides; cobalt; nickel; microstructure; metals; hardness

    Como referenciar este item
    Icon

  • IPEN-DOC 18679

    GUIMARAES, N.M.; REIS, D.A.P.; MOURA NETO, C.; COELHO, G.C.; COUTO, A.A. . Modeling analyze from titanium alloy. Defect and Diffusion Forum, v. 326-328, p. 515-519, 2012.

    Palavras-Chave: titanium alloys; simulation; thermodynamics; phase diagrams

    Como referenciar este item
    Icon

  • IPEN-DOC 28599

    GUIMARAES, M.A.; SANTOS, G.A. dos; NASCIMENTO, M.S. ; TERAM, R.; SANTOS, V.T. dos; SILVA, M.R. da; COUTO, A.A. ; MACHADO, I.F.. Study on the wear of cutting-tools used in dry machining of Cu-10wt%Al-5wt%Ni-5wt%Fe alloy. Defect and Diffusion Forum, v. 413, p. 194-200, 2021. DOI: 10.4028/www.scientific.net/DDF.413.194

    Abstract: Aluminium bronze alloys are special copper alloys that have a machinability rate from 20 to 40% compared to free cutting brasses, so the cutting parameters and type of tools suitable for machining of these materials may be very different for other copper alloys. Also, due to the relative high costs of the raw material, the absence of contamination of the chips by cutting fluids improve its intrinsic resales value and encourage the use of machining process without coolant. The aim of this work is to evaluate the tool wear mechanisms in the finishing machining of the Cu-10wt%Al- 5wt%Ni-5wt%Fe aluminium-bronze alloy with carbide and cermet inserts at different cutting speeds under dry machining condition. The turning of material showed lower surface roughness in higher speed conditions and better dimensional stability at lower speeds. It was observed the formation of continuous chips, but of little volume occupied. The scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS) analyses of tool wear show the adhesion as the main tool wear mechanism, followed by abrasion. At the lower cutting speed, the adhesion wears affected significantly the surface finish, reducing the tool life in comparison to the higher speeds.

    Palavras-Chave: aluminium; bronze; alloys; tools; wear; surface finishing; machining

    Como referenciar este item
    Icon

  • IPEN-DOC 29521

    VICENTE, MARCOS A.A.H.; SILVA, LEONARDO G.A. ; LIMA, NELSON B. ; OLIVEIRA, RENE R. ; BERNUSSI, AYRTON; SARMENTO, BRUNO; BARBOSA, ISABELLA T.F.; MUNHOZ JUNIOR, ANTONIO H.. Synthesis of pseudoboehmite nanoparticles and use in simvastatin drug delivery. Defect and Diffusion Forum, v. 420, p. 141-151, 2022. DOI: 10.4028/p-04240m

    Abstract: Pseudoboehmite is an aluminium compound with a structure similar to that of boehmite. The unit cell of the pseudoboehmite is slightly larger than that of the boehmite because of the greater incorporation of water in the same structure [1]. It has particles of nanometric dimensions and can be synthesized with extremely high purity. Several papers published in the literature show the potential of using this material in the controlled release of drugs, including cancer treatment [2,3]. Using drugs in complexes incorporated into polymer matrices and ceramic gels can lead to adequate control of gastrointestinal absorption when administered orally. Consequently, there is the possibility of promoting a gradual action through the progressive release of the drug, thus increasing its efficiency and reducing dose and toxicity. Previous studies have shown that pseudoboehmite is non-toxic and can be used for drug delivery. During the tests to determine the toxicity of this material, it was observed that the blood glucose content was reduced in mice that took pseudoboehmite by gavage. Since pseudoboehmite is obtained via low-cost inorganic synthesis, different physicochemical characteristics can be incorporated into this high purity medium. The formed structure was evaluated as a drug delivery system to establish a profile of the influence of the physicochemical properties of a molecule in the process of interaction with pseudoboehmite, a drug with recognized pharmacological activity, simvastatin (IUPAC name (1S,3R,7S,8S,8aR)-8-{2-[(2R,4R)-4-hydroxy-6-oxooxan-2-yl]ethyl}-3,7-dimethyl-1,2,3,7,8,8a-hexahydronaphthalen-1-yl 2,2-dimethylbutanoate) was choose. It also emphasizes the importance of pseudoboehmite as a drug carrier, serving as a precursor to new therapeutic systems. The synthesis of pseudoboehmite from ammonium hydroxide and aluminium nitrate was optimized to release simvastatin in vitro. After absorption and hydrolysis in the liver to form the active β-hydroxy acid metabolite, simvastatin acts as a potent reversible, competitive inhibitor of 3-hydroxy-3-methylglutaryl coenzyme A (HMG-CoA) reductase, an early and rate-limiting enzyme in the biosynthesis of cholesterol.

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.