Navegação por assunto "pitting corrosion"
-
LOBO, RAQUEL de M.
; ANDRADE, ARNALDO H.P. de
.
Advances in the understanding of the mechanisms of iodine-induced SCC cracking in zirconium alloys.
In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE,
October 21-25, 2019,
Santos, SP.
Proceedings...
Rio de Janeiro: Associação Brasileira de Energia Nuclear,
2019.
p. 5339-5345.
Abstract:
In pressurized water reactors (PWR) the fuel rod cladding is the first barrier against the spread of
fission
products. It is therefore essential to guarantee its use in the reactor. Sometimes the production of electricity
requires that certain power plants operate in “network monitoring”. The fuel introduced into nuclear power
reactors can then undergo so metimes significant power variations. Following a severe reactor power transient,
clad failure can occur through a stress corrosion phenomenon (SCC), under the combined action of mechanical
stresses and gaseous fission products generated by the fuel pellets. Among those iodine plays a major role, for it
may induce SCC in zircaloy. In the early ages of water cooled reactors (PWRs, BWRs or CANDU), series of
similar failures took place following sharp startups. Today power increase rates as well as instantaneous local
power levels are limited. Indeed, it is well know that cladding failure by iodine induced stress corrosion
cracking (I SCC) may occur under pellet cladding interactions (PCI) conditions during power transients in
PWRs. In this paper we review the advances in the understanding of these SCC cracking mechanisms of the
fuel rod cladding that would then allow better control of the integrity of the clad during the more severe
demands related to the operating conditions of th e PWRs.
Palavras-Chave:
cladding;
cleavage;
computerized tomography;
cracking;
fuel rods;
iodine;
nucleation;
pitting corrosion;
pwr type reactors;
slip;
stress corrosion;
zircaloy 4
LOBO, RAQUEL de M.; ANDRADE, ARNALDO H.P. de.
Advances in the understanding of the mechanisms of iodine-induced SCC cracking in zirconium alloys.
In:
INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE,
October 21-25, 2019,
Santos, SP.
Proceedings...
Rio de Janeiro: Associação Brasileira de Energia Nuclear,
2019.
p. 5339-5345.
Disponível em: http://repositorio.ipen.br/handle/123456789/30719. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
UPADHYAYA, B.R.; ERBAY, A.S.; HOOPER, W.C.; MESQUITA, R.N.
.
Automated monitoring of defects in heat exchanger and steam generator tubing by eddy current test data analysis.
In: PUSEY, H.C. (Ed.); RAO, R.B.K.N. (Ed.) INTERNATIONAL CONGRESS ON CONDITION MONITORING AND DIAGNOSTIC ENGINEERING MANAGEMENT, 13th,
Dec. 3-8, 2000,
Houston, TX, USA.
Proceedings...
Haymarket, VA, USA: MFPT Society, 2000,
2000.
p. 203-211.
Palavras-Chave:
reactor monitoring systems;
heat exchangers;
steam generators;
tubes;
defects;
automation;
eddy current testing;
fuzzy logic;
pitting corrosion;
stress corrosion;
transients;
signals;
functions
UPADHYAYA, B.R.; ERBAY, A.S.; HOOPER, W.C.; MESQUITA, R.N.
Automated monitoring of defects in heat exchanger and steam generator tubing by eddy current test data analysis.
In:
PUSEY, H.C. (ed.); RAO, R.B.K.N. (ed.) INTERNATIONAL CONGRESS ON CONDITION MONITORING AND DIAGNOSTIC ENGINEERING MANAGEMENT, 13th,
Dec. 3-8, 2000,
Houston, TX, USA.
Proceedings...
Haymarket, VA, USA: MFPT Society, 2000,
2000.
p. 203-211.
Disponível em: http://repositorio.ipen.br/handle/123456789/16471. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
CUBAKOVIC, I.A.; AGOSTINHO, S.M.L.; PAES de ANDRADE, A.H.
.
Caracterizacao eletroquimica dos acos inoxidaveis austeniticos do tipo 304, 304L e 316 em aguas naturais contendo ions cloreto e peroxido.
In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 13.; SEMINARIO DE MATERIAIS PARA O SETOR ELETRICO, 6.,
6-9 dez, 1998,
Curitiba, PR.
Anais...
1998.
p. 695-704.
Palavras-Chave:
austenitic steels;
stainless steel-304;
stainless steel-304l;
stainless steel-316;
electric potential;
water;
natural radioactivity;
peroxides;
sodium chlorides;
pitting corrosion;
radioactive waste disposal
CUBAKOVIC, I.A.; AGOSTINHO, S.M.L.; PAES de ANDRADE, A.H.
Caracterizacao eletroquimica dos acos inoxidaveis austeniticos do tipo 304, 304L e 316 em aguas naturais contendo ions cloreto e peroxido.
In:
CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 13.; SEMINARIO DE MATERIAIS PARA O SETOR ELETRICO, 6.,
6-9 dez, 1998,
Curitiba, PR.
Anais...
1998.
p. 695-704.
Disponível em: http://repositorio.ipen.br/handle/123456789/18866. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
BARBOSA, WANESSA
; COSTA, ISOLDA
.
Caracterização e comportamento de corrosão da liga 2098-T351 Al-Cu-Li após diferentes pré-tratamentos de anodização.
In: PROGRAMA INSTITUCIONAL DE BOLSAS DE INICIAÇÃO CIENTÍFICA; SEMINÁRIO ANUAL PIBIC, 26.; SEMINÁRIO ANUAL PROBIC, 17.; SEMINÁRIO ANUAL PIBITI, 10.,
16-17 de dezembro, 2020,
Online.
Resumo expandido...
São Paulo, SP: IPEN-CNEN/SP,
2020.
p. 95-96.
Palavras-Chave:
corrosion;
aluminium alloys;
pitting corrosion;
anodization
BARBOSA, WANESSA; COSTA, ISOLDA.
Caracterização e comportamento de corrosão da liga 2098-T351 Al-Cu-Li após diferentes pré-tratamentos de anodização.
In:
PROGRAMA INSTITUCIONAL DE BOLSAS DE INICIAÇÃO CIENTÍFICA; SEMINÁRIO ANUAL PIBIC, 26.; SEMINÁRIO ANUAL PROBIC, 17.; SEMINÁRIO ANUAL PIBITI, 10.,
16-17 de dezembro, 2020,
Online.
Resumo expandido...
São Paulo, SP: IPEN-CNEN/SP,
2020.
p. 95-96.
Disponível em: http://200.136.52.105/handle/123456789/31763. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
FERNANDES, S.M.C.; CORREA, O.V.
; SOUZA, J.A. de; RAMANATHAN, L.V.
.
A coating to protect spent aluminium-clad research reactor fuel assemblies during extended wet storage.
In: ANNUAL TOPICAL MEETING ON RESEARCH REACTOR FUEL MANAGEMENT, 13th,
March 22-25, 2009,
Vienna, Austria.
Proceedings...
2009.
p. 66-70.
Palavras-Chave:
research reactors;
aluminium alloys;
pitting corrosion;
spent fuels;
coatings;
wet storage
FERNANDES, S.M.C.; CORREA, O.V.; SOUZA, J.A. de; RAMANATHAN, L.V.
A coating to protect spent aluminium-clad research reactor fuel assemblies during extended wet storage.
In:
ANNUAL TOPICAL MEETING ON RESEARCH REACTOR FUEL MANAGEMENT, 13th,
March 22-25, 2009,
Vienna, Austria.
Proceedings...
2009.
p. 66-70.
Disponível em: http://repositorio.ipen.br/handle/123456789/13148. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
FERNANDES, S.M.C.; CORREA, O.V.
; SOUZA, J.A. de; LIMA, N.B. de
; RAMANATHAN, L.V.
; ANTUNES, R.A.; OLIVEIRA, M.C.L. de.
Coatings for increased protection of aluminium clad spent nuclear fuel during long term wet storage.
In: EUROPEAN CORROSION CONGRESS,
September 1-5, 2013,
Estoril, Portugal.
Proceedings...
2013.
Palavras-Chave:
research reactors;
aluminium alloys;
pitting corrosion;
spent fuels;
coatings;
wet storage
FERNANDES, S.M.C.; CORREA, O.V.; SOUZA, J.A. de; LIMA, N.B. de; RAMANATHAN, L.V.; ANTUNES, R.A.; OLIVEIRA, M.C.L. de.
Coatings for increased protection of aluminium clad spent nuclear fuel during long term wet storage.
In:
EUROPEAN CORROSION CONGRESS,
September 1-5, 2013,
Estoril, Portugal.
Proceedings...
2013.
Disponível em: http://repositorio.ipen.br/handle/123456789/16820. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
RAMANATHAN, L.V.
; FERNANDES, S.M.C.
; CORREA, O.V.
; SOUZA, J.A. de
; ANTUNES, R.A.; OLIVEIRA, M.C.L. de.
Coatings for safe long term wet storage of spent Al-clad research reactor fuels.
In: INTERNATIONAL CONFERENCE ON RESEARCH REACTORS: SAFE MANAGEMENT AND EFFECTIVE UTILIZATION,
November 16-20, 2015,
Vienna, Austria.
Proceedings...
Vienna, Austria: International Atomic Energy Agency,
2015.
p. 1-8.
Abstract:
Pitting corrosion of the aluminium cladding of spent research reactor (RR) fuels in wet storage has been observed and the use of conversion coatings to protect the cladding was proposed. A coating prepared by conventional chemical processing as opposed to electrochemical processing is the only option due to constraints related to the shape of the fuel and its high radioactivity. Hence, hydrotalcite (HTC) and boehmite were considered. This paper presents: (a) preparation of hydrotalcite (HTC) coatings from different baths followed by post-coating treatments; (b) corrosion behavior of HTC coated AA 6061 alloy; (c) results of field studies in which uncoated and HTC coated AA 6061 alloy coupons and plates, the latter assembled as a dummy fuel element, were exposed to the IEA-R1 reactor spent fuel basin for extended periods. The laboratory and field tests revealed marked improvements in the corrosion resistance of HTC coated specimens, coupons and plates. The mechanism of corrosion protection is presented.
Palavras-Chave:
cladding;
coatings;
corrosion protection;
corrosion resistance;
iear-1 reactor;
pitting corrosion;
spent fuels;
wet storage
RAMANATHAN, L.V.; FERNANDES, S.M.C.; CORREA, O.V.; SOUZA, J.A. de; ANTUNES, R.A.; OLIVEIRA, M.C.L. de.
Coatings for safe long term wet storage of spent Al-clad research reactor fuels.
In:
INTERNATIONAL CONFERENCE ON RESEARCH REACTORS: SAFE MANAGEMENT AND EFFECTIVE UTILIZATION,
November 16-20, 2015,
Vienna, Austria.
Proceedings...
Vienna, Austria: International Atomic Energy Agency,
2015.
p. 1-8.
Disponível em: http://repositorio.ipen.br/handle/123456789/31216. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
RAMIREZ, ALEXANDER H.
; RAMIREZ, CRISTIAANN H.
; COSTA, ISOLDA
.
Cold rolling effects on the microstructure and pitting resistance of the NBR ISO 5832-1 austenitic stainless steel.
International Journal of Electrochemical Science,
v. 8,
n. 12,
p. 12801-12815,
2013.
Palavras-Chave:
austenitic steels;
corrosion;
cold working;
deformation;
microstructure;
pitting corrosion;
corrosion resistance
RAMIREZ, ALEXANDER H.; RAMIREZ, CRISTIAANN H.; COSTA, ISOLDA.
Cold rolling effects on the microstructure and pitting resistance of the NBR ISO 5832-1 austenitic stainless steel.
International Journal of Electrochemical Science,
v. 8,
n. 12,
p. 12801-12815,
2013.
Disponível em: http://repositorio.ipen.br/handle/123456789/8922. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
MILAGRE, M.X.
; ARAUJO, J.V.
; QUEIROZ, F.M.
; MACHADO, C.S.C.
; COSTA, I.
.
Comparação do comportamento de corrosão da liga convencional AA2024-T351 e da liga Al-Li 2098-T351 / Corrosion behavior of conventional alumïnium alloy AA2024-T351 and Al-LI alloy AA2098-T351.
In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22.,
06-10 de novembro, 2016,
Natal, RN.
Anais...
2016.
p. 6629-6636.
Abstract:
In this work, the localized corrosion behavior of an Al-Li alloy (AA2098-T351) was compared with that of the AA2024-T351 conventional alloy by immersion test in 0.01 mol L-1 NaCl solution. The evolution of localized corrosion in both alloys was monitored by optical microscopy and scanning electron microscopy after several test periods from 2h to 24h. The results showed high susceptibility of the two alloys to pitting from the early hours of immersion. The corrosion mechanism in the two alloys, however, was different. Localized corrosion in the AA2024 alloy was associated with the microcells generation between micrometric precipitates and the matrix leading to superficial attack homogeneously distributed throughout the surface exposed to the corrosive environment. In the AA2098 alloy, however, a severe localized corrosion ascribed in the literature to the presence of phase T1 was also observed besides the localized corrosion type similar to that observed in the AA2024 alloy.
Palavras-Chave:
aluminium alloys;
corrosion resistance;
lithium alloys;
optical microscopy;
pitting corrosion;
scanning electron microscopy;
sodium chlorides
MILAGRE, M.X.; ARAUJO, J.V.; QUEIROZ, F.M.; MACHADO, C.S.C.; COSTA, I.
Comparação do comportamento de corrosão da liga convencional AA2024-T351 e da liga Al-Li 2098-T351.
In:
CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 22.,
06-10 de novembro, 2016,
Natal, RN.
Anais...
2016.
p. 6629-6636.
Disponível em: http://repositorio.ipen.br/handle/123456789/27294. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
MARQUES, R.A.; SALIBA SILVA, A.M.
; ROGERO, S.O.
; MONTEMOR, M.F.; COSTA, I.
.
A comparative study of the corrosion resistance of stainless steels obtained by powder metallurgy techniques for application in dental prosthesis.
Materials Science Forum,
v. 660-661,
p. 617-622,
2010.
Palavras-Chave:
stainless steels;
ferromagnetic materials;
corrosion resistance;
powder metallurgy;
prostheses;
teeth;
simulation;
pitting corrosion
MARQUES, R.A.; SALIBA SILVA, A.M.; ROGERO, S.O.; MONTEMOR, M.F.; COSTA, I.
A comparative study of the corrosion resistance of stainless steels obtained by powder metallurgy techniques for application in dental prosthesis.
Materials Science Forum,
v. 660-661,
p. 617-622,
2010.
Disponível em: http://repositorio.ipen.br/handle/123456789/8141. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
MARQUES, R.A.; SALIBA SILVA, A.M.
; ROGERO, S.O.
; MONTEMOR, M.F.; COSTA, I.
.
A comparative study of the corrosion resistance of stainless steels obtained by powder metallurgy techniques for application in dental prosthesis.
In: INTERNATIONAL LATIN-AMERICAN CONFERENCE ON POWDER TECHNOLOGY, 6th,
Nov. 7-10, 2007,
Buzios, RJ.
Proceedings...
2007.
p. 122-127.
Palavras-Chave:
stainless steels;
ferromagnetic materials;
corrosion resistance;
powder metallurgy;
prostheses;
teeth;
simulation;
pitting corrosion
MARQUES, R.A.; SALIBA SILVA, A.M.; ROGERO, S.O.; MONTEMOR, M.F.; COSTA, I.
A comparative study of the corrosion resistance of stainless steels obtained by powder metallurgy techniques for application in dental prosthesis.
In:
INTERNATIONAL LATIN-AMERICAN CONFERENCE ON POWDER TECHNOLOGY, 6th,
Nov. 7-10, 2007,
Buzios, RJ.
Proceedings...
2007.
p. 122-127.
Disponível em: http://repositorio.ipen.br/handle/123456789/18458. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
VIVEIROS, BARBARA V.G. de
; DONATUS, UYIME
; ALENCAR, MAICON C. de
; BERBEL, LARISSA O.
; COSTA, ISOLDA
.
Comparing the corrosion behaviour of AA2050 and AA7050 aluminium alloys by scanning vibrating electrode and scanning ion-selective electrode techniques.
Corrosion Engineering, Science and Technology,
v. 57,
n. 1,
p. 85-96,
2022.
DOI:
10.1080/1478422X.2021.1992132
Abstract:
The susceptibility to localised corrosion of the high strength alloys, AA2050-T84 and AA7050-T7451, used in the aerospace industry, was investigated in this study by localised electrochemical techniques, specifically, scanning vibrating electrode technique (SVET) and scanning ion-selective electrode technique (SIET), in 0.005 mol L−1 NaCl solution. The study was initially carried out using both alloys individually and then, coupling the two alloys and evaluating the effect of galvanic coupling between them. The results revealed that the AA2050-T84, being nobler than the AA7050-T7451, presented higher corrosion current density values when tested in isolation and the depth of corrosion penetration was significantly deeper in the AA2050-T84 alloy than in the AA7050-T7451. However, galvanic coupling of the two alloys resulted in cathodic protection of the AA2050-T84 alloy and a reduction in corrosion current densities on both alloys.
Palavras-Chave:
aluminium alloys;
corrosion resistance;
intergranular corrosion;
pitting corrosion;
coupling;
electrochemical corrosion;
electrodes;
ion-selective electrodes
VIVEIROS, BARBARA V.G. de; DONATUS, UYIME; ALENCAR, MAICON C. de; BERBEL, LARISSA O.; COSTA, ISOLDA.
Comparing the corrosion behaviour of AA2050 and AA7050 aluminium alloys by scanning vibrating electrode and scanning ion-selective electrode techniques.
Corrosion Engineering, Science and Technology,
v. 57,
n. 1,
p. 85-96,
2022.
DOI:
10.1080/1478422X.2021.1992132.
Disponível em: http://repositorio.ipen.br/handle/123456789/33038. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
DONATUS, UYIME
; VIVEIROS, BARBARA V.G. de
; ALENCAR, MAICON C. de
; FERREIRA, RAPHAEL O.; MILAGRE, MARIANA X.
; COSTA, ISOLDA
.
Correlation between corrosion resistance, anodic hydrogen evolution and microhardness in friction stir weldment of AA2198 alloy.
Materials Characterization,
v. 144,
p. 99-112,
2018.
DOI:
10.1016/j.matchar.2018.07.004
Abstract:
Correlation between corrosion resistance, anodic hydrogen evolution and microhardness in the friction stir weldment of AA2198-T851 alloy has been investigated. Different microscopy techniques, scanning vibrating electrode technique (SVET) and potentiodynamic polarization tests were employed in the investigation. Unlike other 3rd generation Al-Cu-Li alloys where the regions that are most susceptible to corrosion are always within the weld region, the results reveal that the parent material is the most susceptible in this case. There is a direct correlation between corrosion resistance, anodic hydrogen evolution and microhardness in the weldment, and the T1 phase is associated with the direct correlation.
Palavras-Chave:
aluminium alloys;
corrosion resistance;
friction;
microhardness;
pitting corrosion;
polarization;
welded joints
DONATUS, UYIME; VIVEIROS, BARBARA V.G. de; ALENCAR, MAICON C. de; FERREIRA, RAPHAEL O.; MILAGRE, MARIANA X.; COSTA, ISOLDA.
Correlation between corrosion resistance, anodic hydrogen evolution and microhardness in friction stir weldment of AA2198 alloy.
Materials Characterization,
v. 144,
p. 99-112,
2018.
DOI:
10.1016/j.matchar.2018.07.004.
Disponível em: http://repositorio.ipen.br/handle/123456789/29299. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
NUNES, P.C.R.; RAMANATHAN, L.V.
.
Corrosao aquosa de materiais compositos a base de aluminio.
In: 10o. CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS,
6-10 de dezembro, 1992,
Aguas de Lindoia, SP.
1992.
p. 319-321.
Palavras-Chave:
composite materials;
aluminium alloys;
pitting corrosion
NUNES, P.C.R.; RAMANATHAN, L.V.
Corrosao aquosa de materiais compositos a base de aluminio.
In:
10o. CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS,
6-10 de dezembro, 1992,
Aguas de Lindoia, SP.
1992.
p. 319-321.
Disponível em: http://repositorio.ipen.br/handle/123456789/14567. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
COSTA, I.
; KOLOSOSKI, J.; SILVA, A.C.N..
Corrosao de chapas de aco inoxidavel AISI 420.
In: 48o. CONGRESSO ANUAL DA ASSOCIACAO BRASILEIRA DE METALURGIA E MATERIAIS,
25-28 de julho, 1993,
Rio de Janeiro, RJ.
Resumo...
1993.
p. 359.
Palavras-Chave:
stainless steels;
martensitic steels;
corrosion;
pitting corrosion
COSTA, I.; KOLOSOSKI, J.; SILVA, A.C.N.
Corrosao de chapas de aco inoxidavel AISI 420.
In:
48o. CONGRESSO ANUAL DA ASSOCIACAO BRASILEIRA DE METALURGIA E MATERIAIS,
25-28 de julho, 1993,
Rio de Janeiro, RJ.
Resumo...
1993.
p. 359.
Disponível em: http://repositorio.ipen.br/handle/123456789/21366. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
DONATUS, UYIME
; FERREIRA, RAPHAEL O.; MOGILI, NAGA V.V.; VIVEIROS, BARBARA V.G. de
; MILAGRE, MARIANA X.
; COSTA, ISOLDA
.
Corrosion and anodizing behaviour of friction stir weldment of AA2198- T851 Al-Cu-Li alloy.
Materials Chemistry and Physics,
v. 219,
p. 493-511,
2018.
DOI:
10.1016/j.matchemphys.2018.08.053
Abstract:
Anodizing behaviour of AA2198-T851 friction stir weldment and the corrosion behaviour of unpolished and
polished weldments of the alloy have been investigated. Electrochemical and microscopic techniques were
employed in the study. The results revealed that the manufacturing-process induced near-surface deformed layer
significantly affected the corrosion behaviour of the weldment. Thus, the corrosion behaviour of the weldment in
the polished condition (which is the common practice) was different from that of the unpolished one due to the
presence of near-surface deformed layer. Anodizing as a corrosion protection method for the weldment caused
the formation of pronounced non-uniform oxide layer thicknesses across the weld zones. This was because the
weldment oxidized at a higher rate compared with the parent material (PM) due to an increased proportion of Li
in solid solution in the stir zone of the weldment.
Palavras-Chave:
chemical reactions;
corrosion;
anodization;
aluminium alloys;
friction welding;
pitting corrosion;
surface properties;
lithium alloys;
copper alloys;
microstructure
DONATUS, UYIME; FERREIRA, RAPHAEL O.; MOGILI, NAGA V.V.; VIVEIROS, BARBARA V.G. de; MILAGRE, MARIANA X.; COSTA, ISOLDA.
Corrosion and anodizing behaviour of friction stir weldment of AA2198- T851 Al-Cu-Li alloy.
Materials Chemistry and Physics,
v. 219,
p. 493-511,
2018.
DOI:
10.1016/j.matchemphys.2018.08.053.
Disponível em: http://repositorio.ipen.br/handle/123456789/29418. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
RAMANATHAN, LALGUDI V.
.
Corrosion and protection of spent Al-clad research reactor fuel during extended wet storage.
In: INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE; MEETING ON NUCLEAR APPLICATIONS, 9th; MEETING ON REACTOR PHYSICS AND THERMAL HYDRAULICS, 16th; MEETING ON NUCLEAR INDUSTRY, 1st,
September 27 - October 2, 2009,
Rio de Janeiro, RJ.
Proceedings...
Sao Paulo: ABEN, 2009,
2009.
Palavras-Chave:
aluminium alloys;
aluminium;
cladding;
coatings;
iear-1 reactor;
pitting corrosion;
spent fuel elements;
stainless steels;
water;
wet storage
RAMANATHAN, LALGUDI V.
Corrosion and protection of spent Al-clad research reactor fuel during extended wet storage.
In:
INTERNATIONAL NUCLEAR ATLANTIC CONFERENCE; MEETING ON NUCLEAR APPLICATIONS, 9th; MEETING ON REACTOR PHYSICS AND THERMAL HYDRAULICS, 16th; MEETING ON NUCLEAR INDUSTRY, 1st,
September 27 - October 2, 2009,
Rio de Janeiro, RJ.
Proceedings...
Sao Paulo: ABEN, 2009,
2009.
Disponível em: http://repositorio.ipen.br/handle/123456789/16518. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
NUNES, P.C.R.; RAMANATHAN, L.V.
.
Corrosion behavior of alumina/Al and Sic/Al metal matrix composites.
In: 12th INTERNATIONAL CORROSION CONGRESS,
September 19-24, 1993,
Houston, Tex., USA.
1993.
Palavras-Chave:
composite materials;
reinforced materials;
pitting corrosion
NUNES, P.C.R.; RAMANATHAN, L.V.
Corrosion behavior of alumina/Al and Sic/Al metal matrix composites.
In:
12th INTERNATIONAL CORROSION CONGRESS,
September 19-24, 1993,
Houston, Tex., USA.
1993.
Disponível em: http://repositorio.ipen.br/handle/123456789/14991. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
RAMANATHAN, L.
; HADDAD, R.; ADELFANG, P.; RITCHIE, I..
Corrosion of aluminium-clad spent research reactor fuel in wet storage.
In: INTERNATIONAL TOPICAL MEETING ON RESEARCH REACTOR FUEL MANAGEMENT, 10th,
April 30 - May 3, 2006,
Sofia, Bulgaria.
Proceedings...
2006.
Palavras-Chave:
spent fuels;
research reactors;
wet storage;
aluminium alloys;
corrosion;
pitting corrosion;
stainless steels;
water
RAMANATHAN, L.; HADDAD, R.; ADELFANG, P.; RITCHIE, I.
Corrosion of aluminium-clad spent research reactor fuel in wet storage.
In:
INTERNATIONAL TOPICAL MEETING ON RESEARCH REACTOR FUEL MANAGEMENT, 10th,
April 30 - May 3, 2006,
Sofia, Bulgaria.
Proceedings...
2006.
Disponível em: http://repositorio.ipen.br/handle/123456789/13770. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
BENDERESKAYA, O.S.; DE, P.K.; HADDAD, R.; HOWELL, J.P.; JOHNSON JUNIOR, A.B.; LAOHAROJANAPHAND, S.; LUO, S.; RAMANATHAN, L.V.
; RITCHIE, I.; HUSSAN, N.; VIDOWSKY, I.; YAKOVLEV, V..
Corrosion of research reactor AL-CLAD spent fuel in water.
In: INTERNATIONAL MEETING ON REDUCED ENRICHMENT FOR RESEARCH AND TEST REACTORS, 24th,
Nov. 3-8, 2002,
San Carlos de Bariloche, Argentina.
2002.
p. 779-795.
Palavras-Chave:
cladding;
coordinated research programs;
corrosion resistance;
crevice corrosion;
iaea;
pitting corrosion;
spent fuel elements
BENDERESKAYA, O.S.; DE, P.K.; HADDAD, R.; HOWELL, J.P.; JOHNSON JUNIOR, A.B.; LAOHAROJANAPHAND, S.; LUO, S.; RAMANATHAN, L.V.; RITCHIE, I.; HUSSAN, N.; VIDOWSKY, I.; YAKOVLEV, V.
Corrosion of research reactor AL-CLAD spent fuel in water.
In:
INTERNATIONAL MEETING ON REDUCED ENRICHMENT FOR RESEARCH AND TEST REACTORS, 24th,
Nov. 3-8, 2002,
San Carlos de Bariloche, Argentina.
2002.
p. 779-795.
Disponível em: http://repositorio.ipen.br/handle/123456789/15829. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
Buscar no repositório
Navegar
Minha conta
Visualizar
A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.
✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do
Buscar no Repositório
, isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.
✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em
Navegar
✔ Os filtros disponíveis em
Navegar
tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro,
Autores IPEN
apresenta uma relação com os autores vinculados ao IPEN; o
ID Autor IPEN
diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome;
Tipo de acesso
diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.
A opção
Busca avançada
utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.
Exemplo:
Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.
Autor: Maprelian
Título: loss of coolant
Tipo de publicação: Texto completo de evento
Ano de publicação: 2015
✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da
International Atomic Energy Agency – IAEA
, por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.
✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o
significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN,
bibl@ipen.br
.
✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.
✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.
✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo
será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.
✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).
ATENÇÃO!
ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI,
clique aqui.
2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI,
clique aqui.
O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.
Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.