JESUS, E.R.B.; MUCSI, C.S.
; LARA, J.A.C.
; NOGUEIRA, E.J.
; FURLANETTO, V.; ROSSI, J.L.
.
Analysis of the mechanical performance of spot welding on PHS 22MnB5 steel.
In: ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,12.,
20-22 de abril, 2022,
Vitória, ES.
Anais...
Recife, PE: Even3,
2022.
DOI:
10.29327/ECFA2022.487309
Abstract:
The hot pressing hardened steel known as “press hardened steel - PHS” is a steel of extreme importance for the automotive industry. The application of this type of steel in the structure of vehicles promotes the improvement of safety, mass reduction and lower fuel consumption. The increase in the use of this type of steel, culminated in the need to deepen knowledge about the joining processes, more specifically about the electrical resistance spot welding process - RSW, which is one of the most used processes in automotive structural construction. The aim of the present work was the evaluation of the autogenous spot weld of 22MnB5 steel hardened through heat treatment in laboratory scale, simulating the cooling rates used during the hot pressing, commonly used in the automotive industrial practice. Welds were made in two different conditions, with welding parameters in a single step (direct welding) and with parameters considering additional pre and post heating steps. Mechanically, the welds were evaluated through the standardized test called tension shear test. The results showed that, according to the American Welding Society - AWS standard, the performance of the welds meets the minimum requirements required for the group of materials in which 22MnB5 falls.
Palavras-Chave:
hardening;
steels;
automotive industry;
welded joints;
shear properties;
strains;
resistance welding;
spot welding
JESUS, E.R.B.; MUCSI, C.S.; LARA, J.A.C.; NOGUEIRA, E.J.; FURLANETTO, V.; ROSSI, J.L.
Analysis of the mechanical performance of spot welding on PHS 22MnB5 steel.
In:
ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,12.,
20-22 de abril, 2022,
Vitória, ES.
Anais...
Recife, PE: Even3,
2022.
DOI:
10.29327/ECFA2022.487309.
Disponível em: http://repositorio.ipen.br/handle/123456789/33549. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
LARA, J.A.C.
; COUTO, C.P.
; NIZES, A.D.C.; ABBADE, L.
; GONSALEZ, B.
; COLOSIO, M.A.; ROSSI, J.L.
.
Effect of resistance spot welding parameters on the residual stress of automotive ultra high strength steel.
In: SENAFOR, 37th; INTERNATIONAL FORGING CONFERENCE, 21th; NATIONAL SHEET METAL FORMING CONFERENCE, 20th; INTERNATIONAL SHEET METAL FORMING CONFERENCE, 7th; BRDDRG CONGRESS, 4th; INTERNATIONAL CONFERENCE ON MATERIALS AND PROCESSES FOR RENEWABLE ENERGIES – BRAZIL/RS, 7th; INTERNATIONAL CONFERENCE ON SURFACE ENGINEERING IN MATERIAL FORMING,
October 04-06, 2017,
Porto Alegre, RS.
Proceedings...
2017.
Abstract:
Studies on residual stress effect in resistance spot welding (RSW) have not been widely
explored for the new ultra-high strength steels (UHSS), such as, press-hardened steel (PHS)
used for the automotive industry application. The number of PHS parts has been widely
increasing in the vehicle structure, due to its ultra-high tensile strength achieved after the hot
stamping process, which can reach 1500 MPa. This outstanding steel properties is function of
steel grade and is a guaranty for lightweight and safety. Weldability is one of major issues to
allow the large product application in the automotive industry however, the numbers of papers
and works with focus on PHS weldability is still small. The residual stresses in spot welded
joints play an important role in affecting the durability of the joint. It is well known that the
residual stresses may reduce the mechanical properties of the welding joint and contribute to
hydrogen embrittlement effect. This paper has undertaken an experimental survey of residual
stress on 22MnB5 - PHS steel, using X-ray diffraction technique, before any heat treatment, i.e.,
without hot stamping, with variation of the main welding parameters. In general, it was found
that the residual stress results showed a great influence of the resistance spot welding
parameters. The residual stress measures showed levels up to 300 MPa in PHS material, which
can impair the material usage.
LARA, J.A.C.; COUTO, C.P.; NIZES, A.D.C.; ABBADE, L.; GONSALEZ, B.; COLOSIO, M.A.; ROSSI, J.L.
Effect of resistance spot welding parameters on the residual stress of automotive ultra high strength steel.
In:
SENAFOR, 37th; INTERNATIONAL FORGING CONFERENCE, 21th; NATIONAL SHEET METAL FORMING CONFERENCE, 20th; INTERNATIONAL SHEET METAL FORMING CONFERENCE, 7th; BRDDRG CONGRESS, 4th; INTERNATIONAL CONFERENCE ON MATERIALS AND PROCESSES FOR RENEWABLE ENERGIES – BRAZIL/RS, 7th; INTERNATIONAL CONFERENCE ON SURFACE ENGINEERING IN MATERIAL FORMING,
October 04-06, 2017,
Porto Alegre, RS.
Proceedings...
2017.
Disponível em: http://repositorio.ipen.br/handle/123456789/34075. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
LARA, J.A.C.
; COUTO, C.P.
; COLOSIO, M.A.; ROSSI, J.L.
; ABBADE, L.M.
.
Influence of spot welding parameters on Al-Si coated 22MnB5 for automotive application.
SAE Technical Paper,
n. 2017-36-0225,
p. 1-6,
2017.
DOI:
10.4271/2017-36-0225
Abstract:
The application of press hardening steels (PHS) Al-Si coating has
been increasing in body in white vehicles as an approach to meet the
demands of safety and CO2 reduction regulations. The vehicle
structures with PHS largely depend on the integrity and the
mechanical performance of the spots weld. During the spot welding
process, intermetallic phase may appear in function of the chemical
composition of the steel and coating. One of these intermetallics is
the Fe-Al phase which brittleness decreases the strength of the weld
joint. In this study, resistance spot welding (RSW) experiments were
performed in order to evaluate the influence of the welding
parameters of single-lap joints PHS - 22MnB5 steel grade. Welded
samples of the Al-Si coated PHS steel as received, i.e., before any
heat treatment and stamping, were evaluated by means of glow
discharge optical emission spectroscopy (GDOES) technique that
allows a quick and accurate evaluation of the chemical composition
profile along the spot weld thickness. The GDOES results showed
that the squeeze welding parameter has the higher influence on
cupper diffusion at the Al-Si-Fe layer. The pre-burn current and
welding current showed the higher influences in Fe-Al diffusion. The
pulse technique and post-heat treatment had had the lower influences
in Fe-Al diffusion.
Palavras-Chave:
presses;
hardening;
steels;
boron;
coatings;
silicon;
aluminium;
heat treatments
LARA, J.A.C.; COUTO, C.P.; COLOSIO, M.A.; ROSSI, J.L.; ABBADE, L.M.
Influence of spot welding parameters on Al-Si coated 22MnB5 for automotive application.
SAE Technical Paper,
n. 2017-36-0225,
p. 1-6,
2017.
DOI:
10.4271/2017-36-0225.
Disponível em: http://repositorio.ipen.br/handle/123456789/29232. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ABBADE, L.
; LARA, J.A.C.
; COUTO, C.P.
; GONSALEZ, B.
; COLOSIO, M.A.; ROSSI, J.L.
.
Resistance spot welding characterization of press hardened steel.
In: ENCONTRO CIENTÍFICO DE FÍSICA APLICADA, 8.,
4-7 de setembro, 2017,
Vitória, ES.
Anais...
São Paulo, SP: Blucher Proceedings,
2017.
p. 10-13.
DOI:
10.5151/phypro-viii-efa-03
Abstract:
In the automotive industry the resistance spot welding (RSW) is one of the most used processes for joining
steel sheets, being of fundamental importance the quality assurance of this process. In this work, 22MnB5
steel sheets for the hot stamping process, also known as PHS (Press Hardening Steel), were joined by the
technique of resistance spot welding, so that the welding parameters were changed 16 times for the
evaluation of the influence of these parameters on the mechanical properties. By conducting ultrasonic,
tensile and hardness test, followed by metallography, it was possible to identify the characteristics of the
spot weld effect on the material. The results of the tests performed in this work confirmed the difference in
mechanical strength of the thermal zone (ZTA) in relation to the molten zone (ZF). For a certain set of the
parameters it was shown a decrease in the strength of the ZTA and increasing to the weld point, which is
demonstrated in the microstructural analysis and thus justifies the detachment of the weld button of the
base material during tensile testing, i.e., there was a higher strength in the welded area.
Palavras-Chave:
resistance welding;
spot welding;
steels;
hardening
ABBADE, L.; LARA, J.A.C.; COUTO, C.P.; GONSALEZ, B.; COLOSIO, M.A.; ROSSI, J.L.
Resistance spot welding characterization of press hardened steel.
In:
ENCONTRO CIENTÍFICO DE FÍSICA APLICADA, 8.,
4-7 de setembro, 2017,
Vitória, ES.
Anais...
São Paulo, SP: Blucher Proceedings,
2017.
p. 10-13.
DOI:
10.5151/phypro-viii-efa-03.
Disponível em: http://repositorio.ipen.br/handle/123456789/31225. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ABBADE, L.
; LARA, J.A.C.
; ROSSI, A.
; ALENCAR, M.A.
; ROSSI, J.L.
; MUCSI, C.S.
.
Resultados preliminares do estudo da união de chapas de aços dissimilares pela técnica brasagem MIG.
In: ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,11.,
1-4 de dezembro, 2020,
Vitória, ES.
Anais...
São Paulo, SP: Blucher,
2021.
p. 122-126.
DOI:
10.5151/xiecfa-Abbade_Marcelo
Abstract:
A busca em fabricar veículos cada vez mais sustentáveis e seguros, por conta da crise dos recursos naturais e a preocupação com a segurança veicular, fez crescer o uso de novos matérias e métodos de conformação e união dos componentes da carroceria. As propriedades da coluna B determinam a segurança dos passageiros em caso de colisão lateral. A coluna B é constituída por materiais diferentes, e por isso, necessitam de um processo de união adequado. Assim, o objetivo do presente trabalho é realizar a caracterização mecânica da união entre o aço 22MnB5 tratado termicamente (têmpera) e o aço CR4, pela técnica brasagem MIG com adição do arame Cu-Si e o gás de proteção argônio. Os materiais utilizados foram, amostras do aço 22MnB5 revestidas por Al-Si e CR4 revestido por Zinco. A união foi realizada a partir de um projeto de corpo de prova, nomeado de furo oblongo regular. Os ensaios realizados (dureza Vickers e metalografia), se enquadram na norma AWS A5 C3. 3-2008. Os resultados obtidos, demonstraram uma queda na resistência mecânica na zona termicamente afetada pelo calor do aço 22MnB5, isso pode ter ocorrido devido ao aquecimento da região, que apresentou mudanças na microestrutura, porém a dureza desse material ainda é maior que no CR4. Nesse caso é foi possível concluir que mesmo com queda na resistência do aço 22MnB5, em um possível ensaio de tração o destacamento da união ocorreria no CR4, uma vez que a resistência deste material é menor.
Palavras-Chave:
brazing;
automotive industry;
steels;
aluminium base alloys;
silicon alloys
ABBADE, L.; LARA, J.A.C.; ROSSI, A.; ALENCAR, M.A.; ROSSI, J.L.; MUCSI, C.S.
Resultados preliminares do estudo da união de chapas de aços dissimilares pela técnica brasagem MIG.
In:
ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,11.,
1-4 de dezembro, 2020,
Vitória, ES.
Anais...
São Paulo, SP: Blucher,
2021.
p. 122-126.
DOI:
10.5151/xiecfa-Abbade_Marcelo.
Disponível em: http://repositorio.ipen.br/handle/123456789/32315. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
LARA, J.A.C.
; ABBADE, L.
; MUCSI, C.S.
; NIZES, A.D.C.; ROSSI, J.L.
.
Study of Patchwelded Blanks Resistance Spot Welding (RSW) Before Hot Stamping with and without Heat Treatment Parameters.
Materials Research,
v. 26,
Suppl.1,
p. 1-8,
2023.
DOI:
10.1590/1980-5373-MR-2023-0053
Abstract:
In recent years, increasing automotive safety and energy efficiency has become a major concern in the automotive industry. Advanced high-strength steel (AHSS) was chosen for its weight reduction and high mechanical strength for the body in white (BIW). Specifically, it has been used in 22MnB5 steel press hardening type steel (PHS) with patchweld technology, which enables the production of reinforced and structural parts in a single stroke during the hot forming process. This study aimed to evaluate the resistance spot welding parameters for patchweld before hot stamping, considering the minimum and maximum residual stress, while ensuring a welding nugget diameter within the approved range. Microhardness and X-ray diffraction were used to analyze the welding zones for phase identification and residual stress measurements. After five weeks of elapsed time, the spot weld showed cracks that were not seen immediately after welding and were probably due to a high residual stress state.
LARA, J.A.C.; ABBADE, L.; MUCSI, C.S.; NIZES, A.D.C.; ROSSI, J.L.
Study of Patchwelded Blanks Resistance Spot Welding (RSW) Before Hot Stamping with and without Heat Treatment Parameters.
Materials Research,
v. 26,
p. 1-8,
2023.
Suppl.1,
DOI:
10.1590/1980-5373-MR-2023-0053.
Disponível em: http://repositorio.ipen.br/handle/123456789/34357. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ROSSI, A.
; ABBADE, L.
; LARA, J.A.C.
; JESUS, E.R.B.; COLOSIO, M.A.; BARBOSA, L.P.
; ROSSI, J.L.
; MUCSI, C.S.
.
Tensile testing and digital image correlation of 22MnB5 press hardened steel (PHS).
In: ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,11.,
1-4 de dezembro, 2020,
Vitória, ES.
Anais...
São Paulo, SP: Blucher,
2021.
p. 67-74.
DOI:
10.5151/xiecfa-Rossi-A_R
Abstract:
Spot welding is a widely used tool for joining sheets parts in the automotive industry. As 22MnB5 steel has the adequate mechanical strength to withstand lateral impact and rollover stresses, it was chosen for the use in B-pillar. It was observed the need to study the spot welded joints, due to the increased need of the automobile industry in reducing the weight vehicle and increasing the passengers' safety in compliance with Resolution of the National Traffic Council of Brazil - CONTRAN n° 751 on the lateral collision test. The microstructure of this steel, in the as fabricated condition, is basically formed by ferrite and perlite, with a tensile strength limit of 600 MPa. This steel is designed to undergo rapid cooling during hot stamping. After this process, this steel presents a completely martensitic microstructure and tensile strength close to 1500 MPa. This work aimed to investigate the strength of spot welded specimens under different experimental conditions, observing the deformations during the tensile tests. The tests were digitally recorded and the sequenced frames were analyzed using a method called digital image correlation (DIC).
Palavras-Chave:
welding;
resistance welding;
steels;
digital systems;
images;
correlations;
pressing
ROSSI, A.; ABBADE, L.; LARA, J.A.C.; JESUS, E.R.B.; COLOSIO, M.A.; BARBOSA, L.P.; ROSSI, J.L.; MUCSI, C.S.
Tensile testing and digital image correlation of 22MnB5 press hardened steel (PHS).
In:
ENCONTRO CIENTÍFICO DE FÍSICA APLICADA,11.,
1-4 de dezembro, 2020,
Vitória, ES.
Anais...
São Paulo, SP: Blucher,
2021.
p. 67-74.
DOI:
10.5151/xiecfa-Rossi-A_R.
Disponível em: http://repositorio.ipen.br/handle/123456789/32317. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
Buscar no repositório
Navegar
-
Todo o repositório
-
Esta comunidade
Minha conta
Visualizar
A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.
✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do
Buscar no Repositório
, isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.
✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em
Navegar
✔ Os filtros disponíveis em
Navegar
tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro,
Autores IPEN
apresenta uma relação com os autores vinculados ao IPEN; o
ID Autor IPEN
diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome;
Tipo de acesso
diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.
A opção
Busca avançada
utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.
Exemplo:
Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.
Autor: Maprelian
Título: loss of coolant
Tipo de publicação: Texto completo de evento
Ano de publicação: 2015
✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da
International Atomic Energy Agency – IAEA
, por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.
✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN,
bibl@ipen.br
.
✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.
✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.
✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.
✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).
ATENÇÃO!
ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI,
clique aqui.
2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI,
clique aqui.
O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.
Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.