CUESTA, ANA; ICHIKAWA, RODRIGO U.
; LONDONO-ZULUAGA, DIANA; DE LA TORRE, ANGELES G.; SANTACRUZ, ISABEL; TURRILLAS, XAVIER; ARANDA, MIGUEL A.G..
Aluminum hydroxide gel characterization within a calcium aluminate cement paste by combined Pair Distribution Function and Rietveld analyses.
Cement and Concrete Research,
v. 96,
p. 1-12,
2017.
DOI:
10.1016/j.cemconres.2017.02.025
Abstract:
There are many commercially importantmultiphasematerialswhich contain amorphous phases, such as cement
pastes, porcelains, glass-ceramics or pharmaceutical compounds. However, the analysis of amorphous phase(s)
within cement matrices that contain high amounts of crystalline phase(s) is a challenge. Here, we report measurements
of total scattering data quantitatively analyzed by Pair Distribution Function (PDF) minimization
and Rietveld methodology to determine phase compositions including both amorphous and nanocrystalline
phase contents in cement-related samples. Furthermore, laboratory techniques were used to complement the
sample characterization. In addition to five reference materials, the main phase of calcium aluminate cements,
CaAl2O4 hydrated at 50 °C to yield crystalline hydrogarnet, Ca3Al2(OH)12, (43wt%) and nanocrystalline aluminum
hydroxide gel, Al(OH)3·0.1H2O (50wt%)was also investigated. The PDF analyses revealed that the hydroxide gel
has a gibbsite local structurewith an average particle size close to 5 nm. PDF and Rietveld quantitative phase analysis
results fully agree.
Palavras-Chave:
aluminium;
hydroxides;
gels;
x-ray diffraction;
calcium;
aluminates;
cements;
garnets;
amorphous state
CUESTA, ANA; ICHIKAWA, RODRIGO U.; LONDONO-ZULUAGA, DIANA; DE LA TORRE, ANGELES G.; SANTACRUZ, ISABEL; TURRILLAS, XAVIER; ARANDA, MIGUEL A.G.
Aluminum hydroxide gel characterization within a calcium aluminate cement paste by combined Pair Distribution Function and Rietveld analyses.
Cement and Concrete Research,
v. 96,
p. 1-12,
2017.
DOI:
10.1016/j.cemconres.2017.02.025.
Disponível em: http://repositorio.ipen.br/handle/123456789/27836. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
CALLIGARIS, GUILHERME A.; FRANCO, MARGARETH K.K.D.
; ALDRIGE, LAURENCE P.; RODRIGUES, MICHELLE S.; BERALDO, ANTONIO L.; YOKAICHIYA, FABIANO
; TURRILLAS, XAVIER; CARDOSO, LISANDRO P..
Assessing the pozzolanic activity of cements with added sugar cane straw ash by synchrotron X-ray diffraction and Rietveld analysis.
Construction and Building Materials,
v. 98,
p. 44-50,
2015.
Palavras-Chave:
sugar cane;
straw;
ashes;
caking power;
thermodynamic activity;
x-ray diffraction;
heat treatments;
synchrotrons;
quantitative chemical analysis;
portland cement;
waste management
CALLIGARIS, GUILHERME A.; FRANCO, MARGARETH K.K.D.; ALDRIGE, LAURENCE P.; RODRIGUES, MICHELLE S.; BERALDO, ANTONIO L.; YOKAICHIYA, FABIANO; TURRILLAS, XAVIER; CARDOSO, LISANDRO P.
Assessing the pozzolanic activity of cements with added sugar cane straw ash by synchrotron X-ray diffraction and Rietveld analysis.
Construction and Building Materials,
v. 98,
p. 44-50,
2015.
Disponível em: http://repositorio.ipen.br/handle/123456789/25324. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ICHIKAWA, RODRIGO U.
; PARRA, JOAO P.R.L.L.; VALLCORBA, ORIOL; PERAL, INMA; YOSHITO, WALTER K.
; SAEKI, MARGARIDA J.; TURRILLAS, XAVIER; MARTINEZ, LUIS G..
Cation distribution of Mn-Zn ferrite nanoparticles using pair distribution function analysis and resonant X-ray scattering.
EPL,
v. 124,
n. 5,
p. 56001-p1 - 56001-p5,
2018.
DOI:
10.1209/0295-5075/124/56001
Abstract:
Mn-Zn ferrite nanoparticles were synthesized by chemical co-precipitation method
and analysed using X-ray synchrotron diffraction data. Pair distribution function (PDF) analysis
was used to probe the local structure and revealed that the first-neighbour distances of Fe-Fe and
Mn-Zn in the 3.0 up to 3.5˚A range are different from the ones usually reported in the literature.
For the sample with the best magnetic behaviour, resonant X-ray scattering (RXS) using three
energies close to the absorption edges of Mn, Zn and Fe was applied to determine the cation
distribution which explained the previous result from PDF analysis.
Palavras-Chave:
nanoparticles;
distribution functions;
scattering;
x-ray diffraction;
ferrite;
zinc compounds;
manganese compounds;
magnetic resonance;
nmr imaging;
images
ICHIKAWA, RODRIGO U.; PARRA, JOAO P.R.L.L.; VALLCORBA, ORIOL; PERAL, INMA; YOSHITO, WALTER K.; SAEKI, MARGARIDA J.; TURRILLAS, XAVIER; MARTINEZ, LUIS G.
Cation distribution of Mn-Zn ferrite nanoparticles using pair distribution function analysis and resonant X-ray scattering.
EPL,
v. 124,
n. 5,
p. 56001-p1 - 56001-p5,
2018.
DOI:
10.1209/0295-5075/124/56001.
Disponível em: http://repositorio.ipen.br/handle/123456789/29931. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ROSSETTO, CLEUSA M.; ICHIKAWA, RODRIGO U.
; MARTINEZ, LUIS G.
; CAREZZATO, GERALDO L.
; CARVALHO, ALEXANDRE M.G.; TURRILLAS, XAVIER.
In situ hydration of sulfoaluminate cement mixtures monitored by synchrotron X-Ray diffraction.
Materials Science Forum,
v. 930,
p. 153-157,
2018.
DOI:
10.4028/www.scientific.net/MSF.930.153
Abstract:
Mixtures of calcium sulfoaluminate and Portland clinkers with gypsum were hydrated
with deionized water. The pastes were introduced in 0.7 mm borosilicate capillary tubes and kept at
40 ºC while diffraction patterns were collected every 35 s for approximately 3 hours with a
monochromatic radiation of 12 keV at the XRD1 beamline of the Laboratório Nacional de Luz
Síncrotron (LNLS) in Campinas, SP - Brazil. The main crystalline phases (C2S, C3S, ettringite,
ye’elemite and gypsum) involved in the hydration were quantified by Rietveld analysis. The most
noticeable fact was the absence of portlandite as a crystalline precipitate, most likely due to the
capture of calcium ions to form ettringite.
Palavras-Chave:
hydration;
aluminates;
cements;
portland cement;
x-ray diffraction;
synchrotrons;
calcium sulfates
ROSSETTO, CLEUSA M.; ICHIKAWA, RODRIGO U.; MARTINEZ, LUIS G.; CAREZZATO, GERALDO L.; CARVALHO, ALEXANDRE M.G.; TURRILLAS, XAVIER.
In situ hydration of sulfoaluminate cement mixtures monitored by synchrotron X-Ray diffraction.
Materials Science Forum,
v. 930,
p. 153-157,
2018.
DOI:
10.4028/www.scientific.net/MSF.930.153.
Disponível em: http://repositorio.ipen.br/handle/123456789/29342. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ICHIKAWA, RODRIGO U.
; LINHARES, HORACIO M.S.M.D.; PERAL, INMA; BALDOCHI, SONIA L.
; RANIERI, IZILDA M.
; TURRILLAS, XAVIER; MARTINEZ, LUIS G.
.
Insights into the local structure of Tb-doped KY3F10 nanoparticles from Synchrotron X‑ray Diffraction.
ACS Omega,
v. 02,
n. 08,
p. 5128-5136,
2017.
DOI:
10.1021/acsomega.7b00668
Abstract:
Pure and Tb-doped nanocrystalline KY3F10
specimens were synthesized by coprecipitation, and portions
of the samples underwent further heat treatment at 600 °C in a
fluorinated atmosphere. Synchrotron X-ray diffraction patterns
acquired at 30 keV allowed to determine both long- and shortrange
ordered structures by Rietveld and pair distribution
function (PDF) analyses, respectively. PDF examination of the
as-synthesized sample allowed to discern a slight deviation
from the basic cubic building unit because the Y−F bond lengths could be explained in S.G. I4/mmm with cell parameters a =
8.1520(9) Å and c = 11.5876(29) Å, whereas Rietveld analysis could equally well fit both the cubic and tetragonal descriptions for
the heat-treated specimens. Also, PDF revealed that the as-synthesized sample exhibited less structural coherence than the heattreated
one.
Palavras-Chave:
doped materials;
nanoparticles;
x-ray diffraction;
nanocrystals;
synchrotrons
ICHIKAWA, RODRIGO U.; LINHARES, HORACIO M.S.M.D.; PERAL, INMA; BALDOCHI, SONIA L.; RANIERI, IZILDA M.; TURRILLAS, XAVIER; MARTINEZ, LUIS G.
Insights into the local structure of Tb-doped KY3F10 nanoparticles from Synchrotron X‑ray Diffraction.
ACS Omega,
v. 02,
n. 08,
p. 5128-5136,
2017.
DOI:
10.1021/acsomega.7b00668.
Disponível em: http://repositorio.ipen.br/handle/123456789/28515. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ROSSETTO, CLEUSA M.; CAREZZATO, GERALDO L.
; MARTINEZ, LUIS G.
; PECCHIO, MARCELO; TURRILLAS, XAVIER.
Mineralogical analysis of Brazilian Portland cements by the Rietveld method with emphasis on polymorphs M1 and M3 of alite / Análisis mineralógico de cementos Portland de Brasil por el método de Rietveld con énfasis en los polimorfos M1 y M3 de la alita.
Boletin de la Sociedad Espanola de Ceramica y Vidrio,
v. 62,
n. 5,
p. 402-417,
2023.
DOI:
10.1016/j.bsecv.2022.06.005
Abstract:
Eight samples of Portland cement and a clinker provided by the Brazilian Association of
Portland Cement were analysed with different laboratory diffractometers and a synchrotron
instrument to determine the statistical variability in the determination of the mass percentage of the main crystalline phases. Five laboratories participated in the experiment. Data
collection was performed by each laboratory following its own internal procedures for a
standard Rietveld analysis of mineral phases. Both Cu and Mo radiations were used. Reflection geometries—with and without sample rotation—and transmission geometries were
also used. The synchrotron diffraction pattern was acquired from a rotating capillary and
a wavelength of 0.41290 A. ˚ Analysis of all diffraction patterns was performed with the help
of TOPAS Academic v. 6 with the specific purpose of determining the proportions of polymorphs M1 and M3 of alite, since their ratio must be taken into account for the subsequent
development of the mechanical properties of concrete.
Palavras-Chave:
cements;
portland cement;
mineralogy;
crystal structure
ROSSETTO, CLEUSA M.; CAREZZATO, GERALDO L.; MARTINEZ, LUIS G.; PECCHIO, MARCELO; TURRILLAS, XAVIER.
Mineralogical analysis of Brazilian Portland cements by the Rietveld method with emphasis on polymorphs M1 and M3 of alite.
Boletin de la Sociedad Espanola de Ceramica y Vidrio,
v. 62,
n. 5,
p. 402-417,
2023.
DOI:
10.1016/j.bsecv.2022.06.005.
Disponível em: http://repositorio.ipen.br/handle/123456789/34214. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
-
ICHIKAWA, RODRIGO U.
; PARRA, JOAO P.R.L.L.; MARTINS, MURILLO L.; YOSHITO, WALTER K.
; SAEKI, MARGARIDA J.; TURRILLAS, XAVIER; MARTINEZ, LUIS G.
.
Size-strain analysis of iron-excess Mn–Zn ferrite nanoparticles using synchrotron diffraction and its correlation with magnetic saturation and isoelectric pH.
Journal of Nanoscience and Nanotechnology,
v. 18,
n. 8,
p. 5697-5703,
2018.
DOI:
10.1166/jnn.2018.15446
Abstract:
Iron-excess Mn–Zn ferrite nanoparticles were prepared by coprecipitation with sodium hydroxide
(NaOH) at different concentrations (0.1, 0.2, 0.5 and 1.0 mol/L). The results of X-ray diffraction
(XRD) analysis using Whole Powder Pattern Modeling (WPPM) showed that higher concentrations
of NaOH promote crystallite growth and broader dispersion in crystallite sizes. Energy dispersive
X-ray spectroscopy indicates that zinc loss is noticeable when [NaOH] ≥ 0.2 mol/L. XRD revealed
also a significant less-crystalline phase contribution alongside the main peaks of the nanocrystalline
cubic spinel ferrite phase. The less-crystalline fraction is lower for the ferrite obtained with 0.2 mol/L
of NaOH, being about 50% and more than 70% for the other samples. Despite of the less-crystalline
fraction and the excess of iron, no secondary phases were detected. The Warren curves showed
that the concentration of NaOH significantly influences the microstrain in the crystallites, being
smaller for the sample obtained with NaOH at 0.2 mol/L. The sample prepared with this condition
presented the better properties to be used as magnetic tracer in clinical diagnoses combining small
mean crystallite size, low microstrain, which resulted in materials with higher magnetic saturation
and high surface charge under blood pH.
Palavras-Chave:
nanoparticles;
ferrite;
strains;
fourier analysis;
synchrotron radiation;
x-ray diffraction
ICHIKAWA, RODRIGO U.; PARRA, JOAO P.R.L.L.; MARTINS, MURILLO L.; YOSHITO, WALTER K.; SAEKI, MARGARIDA J.; TURRILLAS, XAVIER; MARTINEZ, LUIS G.
Size-strain analysis of iron-excess Mn–Zn ferrite nanoparticles using synchrotron diffraction and its correlation with magnetic saturation and isoelectric pH.
Journal of Nanoscience and Nanotechnology,
v. 18,
n. 8,
p. 5697-5703,
2018.
DOI:
10.1166/jnn.2018.15446.
Disponível em: http://repositorio.ipen.br/handle/123456789/29362. Acesso em: $DATA.
Esta referência é gerada automaticamente de acordo com as normas do estilo IPEN/SP (ABNT NBR 6023) e recomenda-se uma verificação final e ajustes caso necessário.
Como referenciar este item
Buscar no repositório
Navegar
-
Todo o repositório
-
Esta coleção
Minha conta
Visualizar
A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.
✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do
Buscar no Repositório
, isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.
✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em
Navegar
✔ Os filtros disponíveis em
Navegar
tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro,
Autores IPEN
apresenta uma relação com os autores vinculados ao IPEN; o
ID Autor IPEN
diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome;
Tipo de acesso
diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.
A opção
Busca avançada
utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.
Exemplo:
Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.
Autor: Maprelian
Título: loss of coolant
Tipo de publicação: Texto completo de evento
Ano de publicação: 2015
✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da
International Atomic Energy Agency – IAEA
, por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.
✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN,
bibl@ipen.br
.
✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.
✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.
✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.
✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).
ATENÇÃO!
ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI,
clique aqui.
2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI,
clique aqui.
O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.
Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.
A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.
O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.