  • IPEN-DOC 11223

    SCHIAVON, M.A.; YOSHIDA, I.V.P.; BRESSIANI, J.C. ; ACCHAR, W.. Ceramic composites derived from polysiloxane/Al/Nb by AFCOP process. Materials Science Forum, v. 498/499, p. 375-380, 2005.

    Palavras-Chave: ceramics; composite materials; matrix materials; polymers; pyrolysis; aluminium; niobium; siloxanes; microstructure

    Como referenciar este item
    Icon

  • IPEN-DOC 20115

    MUCCILLO, E.N.S. ; GONCALVES, M.D.; GROSSO, R.L. ; MUCCILLO, R. . Characterization of yttrium-doped barium zirconate nanocrystalline powder prepared by spray pyrolysis. Materials Science Forum, v. 798-799, p. 407-412, 2014.

    Palavras-Chave: yttrium; doped materials; barium; zirconates; nanostructures; crystals; powders; sprays; pyrolysis; microstructure

    Como referenciar este item
    Icon

  • IPEN-DOC 11147

    ROCHA, R.M.; GREIL, P.; BRESSIANI, J.C. ; BRESSIANI, A.H.A. . Complex-shaped ceramic composites obtained by machining compact polymer-filter mixtures. Materials Research, v. 8, n. 2, p. 191-196, 2005. DOI: 10.1590/S1516-14392005000200019

    Palavras-Chave: ceramics; composite materials; polymers; precursor; pyrolysis; sample preparation; mixing; aluminium oxides; siloxanes

    Como referenciar este item
    Icon

  • IPEN-DOC 24866

    MACHADO, GLAUSON A.F. ; ROCHA, ROSA M.; BRESSIANI, ANA H.A. . Composites obtained from alumina and polymer derived ceramic. Materials Science Forum, v. 912, p. 141-146, 2018. DOI: 10.4028/www.scientific.net/MSF.912.141

    Abstract: Alumina-mullite composites with low shrinkage can be made by reaction bond using mixtures of alumina, aluminum and silicon carbide. In this work, an alternative route is used to produce alumina composites with low shrinkage. Here alumina samples containing additions of 10 and 20 wt% of a preceramic polymer were warm-pressed and treated in the range of 900 -1500°C to produce alumina based composites. The obtained composites were analyzed by linear shrinkage and compared to pure alumina samples sintered at the same temperature range. It were also evaluated the density variation and crystalline phases formed during heat treatment of alumina composites. Results showed that alumina-silicon oxycarbide and alumina-mullite composites were obtained with lower shrinkage than pure alumina samples.

    Palavras-Chave: composite materials; silicon carbides; polymers; mullite; aluminium oxides; ceramics; pyrolysis

    Como referenciar este item
    Icon

  • IPEN-DOC 09689

    ROCHA, R.M.; GREIL, P.; BRESSIANI, J.C. ; BRESSIANI, A.H.A. . Development and characterisation of Si-Al-O-N-C ceramic composites from polysiloxane-filler mixtures. Materials Science Forum, v. 416/418, p. 505-510, 2003.

    Palavras-Chave: ceramics; composite materials; aluminium; silicon; powders; silicon carbides; fillers; siloxanes; polymers; pyrolysis; aluminium nitrides; aluminium oxides; silicon nitrides

    Como referenciar este item
    Icon

  • IPEN-DOC 25784

    GUILHEN, S.N. ; COLETI, J.; TENORIO, J.A.S.; FUNGARO, D.A. . Influence of adsorption parameters on uranium adsorption capability by biochar derived from macauba coconut residue. Brazilian Journal of Radiation Sciences, v. 7, n. 2A, p. 1-14, 2019. DOI: 10.15392/bjrs.v7i2A.590

    Abstract: Biochar (BC) is a carbon-rich product obtained when biomass is thermally decomposed at relatively low temperatures (under 700ºC) and limited supply of oxygen in a process called pyrolysis. Because of its porous structure, charged sur-face and surface functional groups, BC exhibits a great potential as an adsorbent. Its characteristics strongly depend on the feedstock and the pyrolysis conditions. The aim of this study was to evaluate the adsorption potential for the remov-al of uranium, U(VI) from aqueous solutions using BC obtained through slow pyrolysis of the macauba coconut endo-carp. The influence of parameters such as pH, sorbent dose and initial concentration on the adsorption of U(VI) was investigated. The BC obtained at 350 °C (BC350) presented a removal percentage of approx. 80 %, demonstrating its applicability for the treatment of uranium contaminated aqueous solutions.

    Palavras-Chave: adsorption; uranium; chars; biological materials; concentration ratio; coconut palms; temperature dependence; waste water; pyrolysis; ph value

    Como referenciar este item
    Icon

  • IPEN-DOC 27191

    REDÍGOLO, M.M. ; ALVES, M.V.R. ; REIS, T.R. dos; CARNEIRO, T.C.; COSTA, I. ; BUSTILLOS, O.V. . Material characterization of exudates from Brazilian contemporary oil painting by FTIR, Py-GC/MS and SEM-EDS. Asian Journal of Science and Technology, v. 11, n. 4, p. 10880-10882, 2020.

    Abstract: Contemporary art has employed almost every single synthetic material created by man. Nonetheless, the appeal of oil paint is still present at most public and private collections. Oil paint manufacture has evolved over time along with its formulation and conservation concerns. A reported problem is the formation of exudates on contemporary oil paintings. This work aims to characterize exudates from the Brazilian oil painting “Três pessoas” (1999), by Marina Saleme. Characterization was carried out by Fourier transform infrared spectroscopy, pyrolysis coupled to gas chromatography and mass spectrometry and scanning electron microscopy coupled to energy dispersive x-ray fluorescence spectrometry. Results indicate that exudates are formed by the oxidation of linseed oil and formation of dicarboxylic acids. This process is aided by the formation of zinc stearate in the paint film.

    Palavras-Chave: synthetic materials; cultural objects; chemical composition; fourier transformation; spectroscopy; infrared spectra; gas chromatography; mass spectroscopy; pyrolysis; scanning electron microscopy; dispersions; energy

    Como referenciar este item
    Icon

  • IPEN-DOC 11391

    ROCHA, R.M.; SCHEFFLER, M.; GREIL, P.; BRESSIANI, J.C. ; BRESSIANI, A.H.A. . Obtencao de substratos ceramicos no sistema Si-Al-O-N-C empregando polissiloxanos e cargas de Si e Alsub(2)Osub(3) / Ceramic tapes of Si-Al-O-N-C compounds using mixtures of polyssiloxane and Si-Al2O3 fillers. Cerâmica, v. 51, n. 317, p. 42-51, 2005. DOI: 10.1590/S0366-69132005000100009

    Palavras-Chave: ceramics; casting; aluminium; silicon; silicon carbides; fillers; siloxanes; polymers; pyrolysis; aluminium nitrides; aluminium oxides; silicon nitrides; thermogravimetric analysis

    Como referenciar este item
    Icon

  • IPEN-DOC 03131

    KADOI, H.; OIKAWA, H. ; LUGAO, A.B. ; DIAS, L.C.; CASTAGNET, A.C.. Obtencao de tetrafluoroetileno por pirolise do clorodifluorometano. Anais da Associação Brasileira de Química, v. 36/37, n. 1/4, p. 55-62, 1986.

    Palavras-Chave: ethylene; methane; pyrolysis

    Como referenciar este item
    Icon

  • IPEN-DOC 09776

    ROCHA, R.A.; MUCCILLO, E.N.S. . Physical and chemical properties of nanosized powders of gadolinia-doped ceria prepared by the cation complexation technique. Materials Research Bulletin, v. 38, n. 15, p. 1979-1986, 2003.

    Palavras-Chave: ceramics; gadolinium oxides; cerium oxides; solid solutions; chemical preparation; citric acid; complexes; pyrolysis; powders; particle size; chemical properties; physical properties; x-ray diffraction; infrared spectra

    Como referenciar este item
    Icon

  • IPEN-DOC 09659

    SCHEFFLER, M.; DERNOVSEK, O.; SCHWARZE, D.; BRESSIANI, A.H.A. ; BRESSIANI, J.C. ; ACCHAR, W.; GREIL, P.. Polymer/filler derived NbC composite ceramics. Journal of Materials Science, v. 38, n. 24, p. 4925-4931, 2003.

    Palavras-Chave: ceramics; composite materials; niobium carbides; niobium oxides; niobium silicides; polymers; siloxanes; niobium; fillers; pyrolysis; microstructure; mechanical properties

    Como referenciar este item
    Icon

  • IPEN-DOC 22838

    SANTOS, S.C. ; YAMAGATA, C. ; CAMPOS, L.L. ; MELLO-CASTANHO, S.R.H. . Processing, microstructure and thermoluminescence response of biomorphic yttrium oxide ceramics. Ceramics International, v. 42, n. 11, p. 13291-13295, 2016. DOI: 10.1016/j.ceramint.2016.05.136

    Abstract: The present work reports a fast-direct bio-prototyping process using Luffa Cylindrica vegetable sponge to produce biomorphic yttrium oxide ceramics with reticulated-porous architecture and thermoluminescence response. Processing parameters as rheology of yttrium oxide suspensions, bio-template surface treatment and thermal decomposition of bio-template were investigated. Shear thinning suspensions of 30 vol% yttrium oxide with apparent viscosity of 243mPa.s provided a successful impregnation of samples, whereby bio-templates with smooth ceramic layer and hierarchical reticulated architecture were formed. By thermal treatment at 1600 degrees C for 2 h biomorphic yttrium oxide ceramics with porous microstructure and TL response at 150 degrees C and lambda=550 nm were produced. The proposed fast direct bio-prototyping process is suitable for the production of ceramic components with complex shape and demonstrates potential for general applicability to any bio-template. (C) 2016 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

    Palavras-Chave: processing; microstructure; thermoluminescence; yttrium oxides; ceramics; rare earths; rheology; surface treatments; pyrolysis

    Como referenciar este item
    Icon

  • IPEN-DOC 23088

    MOREIRA, RENATA ; ORSINI, ROSELY dos R. ; VAZ, JORGE M. ; PENTEADO, JOSE C. ; SPINACE, ESTEVAM V. . Production of biochar, bio-oil and synthesis gas from cashew nut shell by slow pyrolysis. Waste and Biomass Valorization, v. 8, n. 1, p. 217-224, 2017. DOI: 10.1007/s12649-016-9569-2

    Abstract: Cashew nut shell waste from northeast region of Brazil was characterized and slow pyrolyzed in a simple batch type reactor heated externally by liquefied petroleum gas as fuel. The experiments were performed using nitrogen or air as carrier gases. The properties of biochar, bio-oil and gases products were investigated and potential applications were proposed. Cashew nut shell showed a high heating value of 20.7 MJ kg(-1) that is among the highest found for different types of biomass. Pyrolysis under nitrogen flow showed a yield of solid, liquid and gas products of about 30, 40 and 30 wt%, respectively. Under air flow an increase of gas phase (46 wt%) was observed with a decrease in the production of biochar and, mainly bio-oil. The biochars have high contents of carbon (70-75 wt%) and high heating values in the range of 25-28 MJ kg(-1) presenting suitable properties for use as energy source. Biochars also contain significant quantities of K and minor amounts of Mg, Ca, Cu, Zn and Fe showing potential as fertilizer. The bio-oils showed high heating values of about 32 MJ kg(-1) and are not suitable for use in pure form, but can be used in mixtures with Diesel (42.5 MJ kg(-1)). The gas phase revealed the predominance of CO2 and CO at temperatures lower than 400 degrees C and, above this temperature, there was a preferential formation of H-2 resulting in synthesis gas with different compositions that could be burned to supply heat for the pyrolysis process and/or to produce organic chemicals.

    Palavras-Chave: coal; nuts; synthesis; pyrolysis; agricultural wastes; methane; synthesis gas

    Como referenciar este item
    Icon

  • IPEN-DOC 25816

    GUILHEN, S.N. ; MASEK, O.; ORTIZ, N. ; IZIDORO, J.C. ; FUNGARO, D.A. . Pyrolytic temperature evaluation of macauba biochar for uranium adsorption from aqueous solutions. Biomass and Bioenergy, v. 122, p. 381-390, 2019. DOI: 10.1016/j.biombioe.2019.01.008

    Abstract: This study aims to evaluate the effect of the pyrolytic temperature on the biochar derived from the macauba endocarp for the removal of uranium (VI) from aqueous solutions. The endocarp was subjected to six different pyrolytic temperatures, ranging from 250 °C to 750 °C. The biochars obtained at each temperature were evaluated for their adsorption capacities (“q”). The highest adsorption capacities were obtained for the biochar produced at 250 °C (BC250), followed by the one obtained at 350 °C (BC350), with removal efficiencies of 86% and 80%, respectively. The best condition was achieved when the endocarp was subjected to temperatures between 300 and 350 °C, at which it was possible to obtain a satisfactory balance among adsorption capacity, gravimetric yield and fixed carbon content. This characteristic, combined with the high removal efficiency, points to an ideal working temperature of 350 °C. Elemental analysis showed a decrease of the H/C and O/C ratios when higher pyrolytic temperatures were applied, indicating an inverse relationship between the carbonization and the surface polar functional groups, which were likely responsible for an increased adsorptive capacity in biochars produced at lower temperatures. Both FTIR and XPS analysis indicated that oxygen-containing groups such as hydroxyls and carboxylic acids were involved with the binding of uranyl ions.

    Palavras-Chave: biomass; carbon; pyrolysis; pyrolytic carbon; temperature dependence; radioactive wastes; uranium; adsorption; coconut palms

    Como referenciar este item
    Icon

  • IPEN-DOC 09654

    DERNOVSEK, O.; BRESSIANI, J.C. ; BRESSIANI, A.H.A. ; ACCHAR, W.; GREIL, P.. Reaction bonded niobium carbide ceramics from polymer-filler mixtures. Journal of Materials Science, v. 35, n. 9, p. 2201-2207, 2000.

    Palavras-Chave: ceramics; composite materials; niobium carbides; polymers; siloxanes; niobium; aluminium oxides; fillers; pyrolysis; microstructure; phase diagrams; mechanical properties

    Como referenciar este item
    Icon

  • IPEN-DOC 11909

    CAMPOS, M. de ; MULLER, F.A.; BRESSIANI, A.H.A. ; BRESSIANI, J.C. ; GREIL, P.. Sonochemical synthesis of calcium phosphate powders. Journal of Materials Science: Materials in Medicine, v. 18, p. 669-675, 2007.

    Palavras-Chave: calcium phosphates; apatites; powders; synthesis; pyrolysis; coatings; implants

    Como referenciar este item
    Icon

  • IPEN-DOC 08204

    RAMBO, C.R.; MARTINELLI, J.R. . Synthesis and characterization of SiC from bamboo. Key Engineering Materials, v. 189/191, p. 9-15, 2001.

    Palavras-Chave: ceramics; silicon carbides; fibers; bamboo; pyrolysis; microstructure; deformation

    Como referenciar este item
    Icon

  • IPEN-DOC 09778

    ROCHA, R.A.; MUCCILLO, E.N.S. . Synthesis and thermal decomposition of a polymeric precursor of the Lasub(2)Mosub(2)Osub(9) compound. Chemistry of Materials, v. 15, n. 22, p. 4268-4272, 2003.

    Palavras-Chave: molybdates; lanthanum compounds; powders; chemical preparation; citric acid; glycols; polymerization; polymers; pyrolysis; thermal analysis; fourier transform spectrometers; infrared spectra

    Como referenciar este item
    Icon

  • IPEN-DOC 19197

    GOUVEIA, DEIBY S.; ROSENHAIM, RAUL; GUEDES JUNIOR, SEVERINO J.; LONGO, ELSON ; SOUZA, ANTONIO G. de; SANTOS, IEDA M.G. dos. The characterization of Cosub(x)Znsub(7-x)Sbsub(2)Osub(12) spinel obtained by the Pechini method. Materials Research, v. 8, n. 2, p. 213-219, 2005. DOI: 10.1590/S1516-14392005000200023

    Palavras-Chave: spinels; zinc; antimony; oxides; sintering; stoichiometry; pyrolysis; cobalt; spectroscopy

    Como referenciar este item
    Icon

  • IPEN-DOC 12826

    MIRANDA JUNIOR, P.; MADUAR, M.F. ; SCHPECTOR, J.Z.; MATOS, J.R.. Thermal decomposition and structural study of lanthanide complexes with trans-1,3-dithiane-1,3-dioxide. Journal of Thermal Analysis and Calorimetry, v. 87, n. 3, p. 793-795, 2007.

    Palavras-Chave: rare earths; pyrolysis; x-ray diffraction

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.