  • IPEN-DOC 29234

    BASTOS, VANDERLEI M. . O clinching e a solda a ponto em aço avançado bifásico de 1,3 GPa de resistência mecânica / Clinching and spot welding in 1.3 GPa advanced dual phase steel . 2022. Dissertação (Mestrado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 66 p. Orientador: Jesualdo Luiz Rossi. DOI: 10.11606/D.85.2022.tde-19102022-170258

    Abstract: No campo de materiais para o setor automotivo, o uso do aço avançado de primeira geração bifásico de 1,3 GPa de resistência mecânica, cuja microestrutura ferrita/martensita confere ultra-alta resistência à tração, pode ser soldado a ponto por resistência elétrica ou unido à frio por conformação plástica e ancoramento (clinching). Algo benéfico é que isto pode ser executado com equipamentos já existentes coadunando para a construção leve. A aplicação do aço avançado de primeira geração bifásico 1,3 GPa de até 1,50 mm de espessura se mostra atrativa para substituir componentes obtidos por estampagem a quente no setor automotivo como barras de proteção lateral, reforços no assoalho e outros componentes relevantes no sistema de gerenciamento da segurança ativa. O presente trabalho visou correlacionar aspectos das uniões por clinching e por solda a ponto por resistência elétrica, quanto à resistência à tração para cisalhamento e para destacamento de corpos de prova preparados em corte por laser. As alterações na região de ancoramento do clinching e da zona afetada pelo calor na solda a ponto foram avaliadas em termos microestruturais e de microdureza. As cargas observadas durante os ensaios de destacamento do clinching com ruptura completa da região de estricção ou zona de estricção se mostraram mais elevadas do que quando ocorreu o desenbricamento da união mecânica. Quanto à solda ponto, apesar das variações adicionadas pelo processo térmico como queda da microdureza e da ruptura na região subcrítica no ensaio de resistência ao destacamento, ainda assim a resistência mecânica à ruptura foi 62% superior ao clinching na média. Os resultados permitiram concluir que, nas condições experimentais do presente trabalho, o clinching é exequível para materiais de ultra-alta resistência e permitiu uma correlação de 3 clinchings para cada 2 pontos de solda para ensaio quase estático.

    Palavras-Chave: sheets; steels; duality; phase transformations; resistance welding; joining; strength functions; mechanical properties; materials working

    Como referenciar este item
    Icon

  • IPEN-DOC 25660

    CASTRO, MICHELE C.B. de . Efeito da nitretação por plasma no comportamento em fadiga da liga Ti-6Al-4V / Nitriding plasma effect on Ti-6Al-4V fatigue behavior . 2018. Dissertação (Mestrado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 86 p. Orientador: Nelson Batista de Lima. Coorientador: Antonio Augusto Couto. DOI: 10.11606/D.85.2019.tde-29032019-094140

    Abstract: A liga Ti-6Al-4V apresenta excelentes propriedades mecânicas, baixa densidade, alta dureza e resistência à corrosão. Entretanto, tratamentos superficiais como a nitretação por plasma são amplamente utilizadas para melhorar a resistência a fadiga desta liga. O objetivo deste trabalho foi tratar termoquimicamente a liga Ti-6Al-4V por meio da nitretação por plasma a fim de verificar a sua influência nas propriedades de fadiga e comparar os resultados obtidos com as não nitretadas. Este tratamento superficial foi realizado com o objetivo de retardar a etapa de nucleação da trinca. A nitretação por plasma foi realizada em temperaturas em torno de 720°C por 4 horas, numa atmosfera de N2, Ar e H2 (5:5:1). Foi realizado um tratamento térmico nas amostras para se obter a microestrutura de Widmanstätten. A temperatura usada foi de 1050°C por 30 minutos. A caracterização microestrutural das amostras nitretadas e não nitretadas foi realizada usando difração de raios X (DRX), microscopia óptica (MO), e microscopia eletrônica de varredura (MEV). Os resultados da difração de raios X das amostras nitretadas mostram a presença de fases: α, β, ε-Ti2N, e δ-TiN e nas amostras não nitretadas as fases α e β. Essas análises revelaram a presença de uma superfície rica em nitretos seguida de uma zona de difusão com nitrogênio na matriz. A rugosidade superficial foi estudada, e foi observada um aumento na rugosidade de 61% após a nitretação. Os testes de fadiga foram realizados em uma máquina de ensaios flexo rotativa, com uma razão de carregamento R=-1 . Os resultados obtidos mostraram que as propriedades de fadiga foram melhoradas após a nitretação por plasma, retardando a etapa de nucleação de trinca.

    Palavras-Chave: titanium alloys; strength functions; weight indicators; corrosion resistant alloys; corrosion fatigue; heat treatments; carbon steels; nitrogen; diffusion; plasma potential; surface hardening; surface treatments

    Como referenciar este item
    Icon

  • IPEN-DOC 19698

    PORTO, KARINA M.B.G. . Efeitos da radiação gama (sup(60)Co) nas principais propriedades físicas e químicas de embalagens compostas por papel grau cirúrgico e filme plástico laminado, destinadas à esterilização de produtos para saúde / Effects of gamma radiation (60Co) on the main physical and chemical properties of health care packaging and their compounds paper and multilayer plastic film, used for health products sterilization . 2013. Dissertação (Mestrado) - Instituto de Pesquisas Energeticas e Nucleares - IPEN-CNEN/SP, São Paulo. 123 p. Orientador: Sueli Ivone Borrely. DOI: 10.11606/D.85.2013.tde-26112013-102247

    Abstract: A radiação gama é uma das tecnologias aplicadas para a esterilização de sistemas de embalagens contendo produtos para a saúde. No processo de esterilização, é fundamental que as propriedades das embalagens sejam mantidas. Neste estudo, duas amostras de embalagens comerciais, no formato de envelope compostas por papel grau cirúrgico de um dos lados e filme plástico laminado do outro, foram irradiadas com raios gama com doses de 25 kGy (taxa de dose de 1,57 kGy/h) e 50 kGy (taxa de dose de 1,48 kGy/h). Uma das amostras de embalagem era constituída por papel de fibras de coníferas e filme plástico laminado de poli(tereftalato de etileno) (PET)/polietileno (PE) e a outra por papel de fibras de coníferas e de folhosas e filme plástico laminado de poli(tereftalato de etileno) (PET)/polipropileno (PP). Os efeitos da radiação nas propriedades físicas e químicas dos papéis e dos filmes plásticos, assim como nas propriedades da embalagem foram estudados. O papel foi o material mais sensível à radiação, sendo a alvura, o pH e as resistências ao rasgo, ao arrebentamento e à tração os parâmetros nos quais foram observadas maiores modificações, em ambas as amostras. Todavia, dos dois tipos de papel, o efeito foi mais pronunciado para a amostra com fibras de conífera e de folhosas. A porosidade dos papéis foi alterada com 50 kGy. No caso dos filmes plásticos, a propriedade com maior modificação foi a resistência à tração, em ambas as amostras. No caso das embalagens, a irradiação diminuiu a resistência da selagem. Os efeitos observados para a dose de 50 kGy foram em média mais pronunciados quando comparados com as modificações nos valores das amostras tratadas com 25 kGy, que é a dose usualmente empregada para esterilização de produtos para a saúde. A dosimetria deste estudo foi realizada nos materiais irradiados com 25 kGy, 40 kGy e 50 kGy, demonstrando sua importância à medida que a variação média para as três doses estudadas foi de 20 %.

    Palavras-Chave: packaging; plastics; polyethylenes; film dosimetry; paper; ethylene; brightness; strength functions; sterilization; health services; physical properties; chemical analysis; gamma radiation; cobalt 60

    Como referenciar este item
    Icon

  • IPEN-DOC 27699

    SILVA, ORELIO L. da . Estudo do polipropileno de alta resistência do fundido (HMSPP) irradiado com carbonato de cálcio/nanopartículas de prata para fins de atividade bactericida / Study of high-strength polypropylene from the melt (HMSPP) irradiated with calcium carbonate/silver nanoparticles for purposes of bactericidal activity . 2020. Dissertação (Mestrado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 80 p. Orientador: Duclerc Fernandes Parra. DOI: 10.11606/D.85.2020.tde-01032021-111908

    Abstract: O carbonato de cálcio (CaCO3) é um mineral importante e abundante em todas as rochas sedimentares utilizadas comercialmente. A casca de ovo de galinha contém 40% de Calcio na forma de CaCO3. Existem vários estudos sobre a influência da adição de carbonato de cálcio nas propriedades físicas e reológicas dos materiais. O objetivo deste trabalho foi avaliar a influência da adição de CaCO3 com nanopartículas de prata (CaCO3/AgNP) em diferentes proporções (0,1 e 0,3%.) nas propriedades de filmes e pellets de HMSPP 12,5 kGy. As cascas lavadas, higienizadas, secas em forno e moídas em um moinho foram caracterizadas para obter o pó de casca de ovo, para uso no presente trabalho. A irradiação em fonte gama foi utilizada para: 1) Preparação de HMSPP, na irradiação de PP a 12,5 kGy; 2) compatibilização CaCO3 / AgNP em HMSPP a 30kGy e 50kGy; 3) Avaliação da estabilidade sob radiação em termos de se as propriedades mecânicas são afetadas ou não na etapa de compatibilidade. Os testes de caracterização realizados para este estudo foram FTIR, DRX, TGA, DSC, bem como teste bactericida. Os resultados indicaram a presença de CaCO3/AgNP nos filmes poliméricos por absorção de FTIR. os picos de prata DRX de 2θ a 38,5° (111) e 44,5° (200) confirmaram a presença de prata no CaCO3. O resultado do DSC indicou que a presença de CaCO3/AgNP nas amostras não alterou a Tm de fusão (155,16°C/CaCO3/Ag 0,1%; 157,52°C/CaCO3/Ag 0,3%) ou a cristalinidade do polímero HMSPP (44,16% e 43,51%), respectivamente, para 0,1 e 0,3%. Além disso, a análise TGA indicou para ambas as amostras de filmes, em diferentes concentrações de CaCO3/AgNP, o mesmo perfil de decomposição, não mostrando influência da radiação ou CaCO3/AgNP na estabilidade térmica dos nanocompósitos.

    Palavras-Chave: eggs; shells; powders; calcium carbonates; silver additions; nanoparticles; strength functions; polypropylene; melt-through; sample preparation; x radiation; x-ray diffraction; scanning electron microscopy; fourier transform spectrometers; thermal gravimetric analysis; dynamical systems; light scattering; infrared spectrometers

    Como referenciar este item
    Icon

  • IPEN-DOC 19065

    GOMES, MAURILIO P. . Investigation on the corrosion mechanisms of pure magnesium and the effect of friction stir welding (FSW) on the corrosion resistance of aluminum alloy 2524-T3 / Investigação dos mecanismos de corrosão do magnésio puro e o efeito da soldagem por fricção e mistura (FSW) na resistência à corrosão da liga de alumínio 2524-T3 . 2021. Tese (Doutorado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 91 p. Orientador: Isolda Costa. DOI: 10.11606/T.85.2021.tde-10032022-151859

    Abstract: Friction stir welding (FSW) is a process that has proven to be quite efficient when it comes to joining high-strength aluminum alloys, for instance AA2524-T3. This can be justified by the fact that welding aluminum alloys by FSW technique allows (i) reduction of aircraft weight by eliminating the rivets commonly used and (ii) the use of different aluminum alloys that have low specific density and high mechanical strength. However, even though FSW allows the joining of metallic parts without their effective fusion, which theoretically would result in a defect-free weld bead, the heat resulting from the friction of the welding tool causes significant microstructural changes. In consequence, it results in variations of mechanical properties and corrosion resistance in the welded region. It was evaluated the FSW welding process influence on the corrosion resistance of the joined 2524-T3 aluminum alloy. Different tools have been used, such as: optical and scanning electron microscopy; open circuit potential and electrochemical impedance spectroscopy measurements; and corrosion tests: agar-agar test, intergranular corrosion test, and exfoliation corrosion test. It was proven by different techniques that the thermomechanically/thermal affect zone interface on the retreating side was the most susceptible to corrosion among all investigated zones. A parallel study was developed regarding the corrosion mechanism of pure magnesium. It has been the subject of a considerable amount of work, and despite its ubiquity and history, it remains controversial. This is mainly due to the presence of the negative difference effect (NDE), which increases hydrogen formation when the magnesium is biased on the anodic domain. We was performed a detailed analysis of the electrochemical impedance spectra obtained for the Mg electrode during immersion in a sodium sulfate solution. A model was proposed which took into account the presence of: (i) a thin oxide film (MgO) which progressively covered the Mg electrode surface, (ii) film-free areas where the Mg dissolution occurs in two consecutive steps, (iii) a thick layer of corrosion products (Mg(OH)2), (iv) an adsorbed intermediate Mg+ads which is responsible for the chemical reaction allowing the NDE to be explained. From the impedance data analyses, various parameters were extracted such as the thin oxide film thickness, the resistivity at the metal/oxide film interface and at the oxide film/electrolyte interface, the active surface area as a function of the exposure time to the electrolyte, the thickness of the thick Mg(OH)2 layer and the kinetic constants of the electrochemical reactions.

    Palavras-Chave: aluminium alloys; magnesium compounds; joining; welding; friction; stirring; microstructure; electrochemical corrosion; corrosion protection; corrosion resistance; mechanical properties; strength functions; impedance; materials testing

    Como referenciar este item
    Icon

  • IPEN-DOC 28044

    HATTORI, CAROLINA S. . Obtenção, caracterização microestrutural e comportamento mecânico de ligas de alumínio da série 7xxx extrudadas para aplicações automotivas / Manufacturing, microstructural characterization, and mechanical behavior of extruded 7xxx series aluminum alloys for automotive applications . 2021. Tese (Doutorado em Tecnologia Nuclear) - Instituto de Pesquisas Energéticas e Nucleares - IPEN-CNEN/SP, São Paulo. 127 p. Orientador: Antonio Augusto Couto. DOI: 10.11606/T.85.2021.tde-18082021-144545

    Abstract: Devido às legislações cada vez mais rígidas quanto a emissão de CO2, uma das opções das montadoras é a utilização de materiais mais leves. Esta questão de leveza trouxe ainda mais atenção para as ligas de alumínio que já são largamente utilizadas na indústria automotiva para diversas aplicações, principalmente as ligas tradicionais da série 5xxx e 6xxx. Diante do cenário de competitividade da indústria, faz-se necessário o desenvolvimento de ligas estruturais de alta resistência mecânica, como as da série 7XXX que são o foco deste estudo. Neste sentido, este trabalho tem como objetivo a obtenção por extrusão de duas novas ligas de alumínio, 7108 e 7046, caracterizar a microestrutura em cada etapa do processo de fabricação e avaliar o comportamento mecânico em tração e em fadiga. Inicialmente, foram vazados tarugos nas duas ligas para posterior desenvolvimento do processo de extrusão, em duas geometrias diferentes de perfil extrudado, visando definir os principais parâmetros do processo e de tratamentos térmicos. As microestruturas dos perfis extrudados das ligas 7108 e 7046 são formadas por partículas de segunda fase ricas em Al-Fe-Si e precipitados finos ricos em Al-Zn-Mg dispersos em matriz de alumínio. O resultado de limite de resistência da liga 7046 apresentou um resultado 36% superior ao da liga 7108, comprovando a influência da quantidade de precipitados formados. Para a liga 7046 todos os níveis de tensão máxima tiveram um desempenho superior nas propriedades de fadiga em relação a liga 7108 e notou-se uma significativa melhoria das propriedades em fadiga em decorrência do polimento dos corpos de prova. Nas superfícies de fratura observa-se uma região de menor área de propagação de trinca e uma região mais extensa de ruptura por sobrecarga mecânica. A região de propagação de trinca é caracterizada por deformação plástica e presença de estrias perpendiculares à direção de crescimento.

    Palavras-Chave: heat treatments; aluminium alloys; zinc; power amplifiers; strength functions; microstructure; mechanical properties; crack propagation; fatigue; fracture mechanics; scanning electron microscopy; materials testing; manufacturing; fabrication; automotive industry

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.