  • IPEN-DOC 23384

    NASCIMENTO, MAURICIO S.; FRANCO, ANTONIO T.R.; NAKAMOTO, FRANCISCO Y.; FRAJUCA, CARLOS; SANTOS, GIVANILDO A. dos; COUTO, ANTONIO A. . An Experimental Study of the Influence of Solidification Thermal Variables upon Microstructure of Al-Si-Cu Alloys. In: BRAZILIAN MRS MEETING, 15th, September 25-29, 2016, Campinas, SP. Abstract... São Carlos, SP: Aptor Software, 2016. p. 1006-1006.

    Abstract: Solidification of metals involves the transformation of the molten metal back into the solid state. The transformation of a liquid into solid is probably the most important phase transformation in applications of science and engineering materials [1, 2]. Solidification structures impact heavily on the products final characteristics and therefore predict microstructure resulting from the solidification thermal variables is essential for the programming process using solidification. The aim of this work is obtain correlations between thermal solidification variables and the microstructure of Al-10wt%Si-2wt%Cu and Al-10wt%Si-5wt%Cu alloys. These alloys were solidified under upward unsteady state heat flow conditions. Heat was directionally extracted only through a watercooled bottom made of steel (SAE 1020). The results include tip growth rate (VL), cooling rate (TR) and primary dendrite arm spacing (λ1) as a function of solidification conditions imposed by the metal/mold system.For both alloys, it is found that the primary dendrite arm spacing decreases with the increase in tip growth rate and cooling rate.

    Como referenciar este item
    Icon

  • IPEN-DOC 26114

    GUIMARAES, MARCOS de A.; SANTOS, GIVANILDO A. dos; AGUIAR, HERBERT C.G. de; SUYAMA, DANIEL I.; SILVA, MARCIO R. da; SANTOS, VINICIUS T. dos; NAKAMOTO, FRANCISCO Y.; FRAJUCA, CARLOS; BATALHA, GILMAR F.; COUTO, ANTONIO A. . Behaviour of PVD multi-layer coating carbide inserts in dry machining of nickel aluminium bronze alloy. In: BRAZILIAN MRS MEETING, 17th, September 16-20, 2018, Natal, RN. Abstract... São Carlos: Aptor Software, 2018. p. 1459-1459.

    Abstract: The aluminium bronze alloys have machinability rate from 20 to 40% compared to free cutting brasses, so the cutting parameters and type of tools suitable for machining of these materials may be very different in comparison with other copper alloys. In this study was evaluated the flank wear rate of multi-layer PVD coating carbide insert in dry machining of nickel aluminium bronze CuAl10Ni5Fe5. The new advanced nano-layer coatings composed of numerous layers of the same, or combinations of different coating types can reduce dramatically the tool flank wear compared to conventional monolayer coatings [1]. The CuAl10Ni5Fe5 alloy was machining by CNC turning at different cutting speeds (cutting conditions). The surface and wear of carbide inserts were analysed by Scanning Electron Microscopy / Energy Dispersive X-Ray Spectroscopy (SEM/EDS). The results showed very small flank wear produced by abrasion on the cutting edge even with the increase of cutting speed from 80 to 450 m/min.

    Como referenciar este item
    Icon

  • IPEN-DOC 23385

    NASCIMENTO, MAURICIO S.; FRANCO, ANTONIO T.R.; NAKAMOTO, FRANCISCO Y.; FRAJUCA, CARLOS; SANTOS, GIVANILDO A. dos; COUTO, ANTONIO A. . Correlation between Microstructure and Mechanical Properties of Al-Si-Cu Alloys Casting. In: BRAZILIAN MRS MEETING, 15th, September 25-29, 2016, Campinas, SP. Abstract... São Carlos, SP: Aptor Software, 2016. p. 1058-1059.

    Abstract: It is well known that mechanical properties depend on solidification structures. The effects of microstructure on metallic alloys properties has been highlighted in various studies and particularly, the influence of grain size and dendrite arm spacing upon the mechanical properties has been reported [1-3]. The aim of this work is obtain correlations between microstructure and the mechanical properties of Al-10wt%Si-2wt%Cu and Al-10wt%Si-5wt%Cu alloys casting. These alloys were solidified under upward unsteady state heat flow conditions. Heat was directionally extracted only through a water-cooled bottom made of steel (SAE 1020). The results include tip growth rate (VL), cooling rate (TR), primary dendrite arm spacing (λ1), ultimate tensile strength (LRT) and yield strength (LE) as a function of solidification conditions imposed by the metal/mold system. In both cases (LRT and LE = 0.2%ε), the finer dendritic arrangement presents superior mechanical properties for the Al-Si-Cu alloys studied.

    Como referenciar este item
    Icon

  • IPEN-DOC 26116

    NASCIMENTO, MAURICIO S.; SANTOS, GIVANILDO A. dos; SOUZA, PAULO E.S.; FRAJUCA, CARLOS; NAKAMOTO, FRANCISCO Y.; SILVA, MARCIO R. da; SANTOS, VINICIUS T. dos; BATALHA, GILMAR F.; COUTO, ANTONIO A. . Correlation between microstructure, thermal parameters and hardness of a directionally solidified Al-Si-Cu alloy. In: BRAZILIAN MRS MEETING, 17th, September 16-20, 2018, Natal, RN. Abstract... São Carlos: Aptor Software, 2018. p. 1123-1124.

    Abstract: Metals solidification involves the transformation of the molten metal back into the solid state. Solidification structures impact heavily on the final product’s characteristics. The microstructure effects on metallic alloys properties have been highlighted in various studies and particularly the dendrite arm spacing influence upon the mechanical properties such as hardness has been reported [1-3]. The aim of this work is to obtain correlations between microstructure and the hardness of Al-10wt%Si-2wt%Cu alloy casting. Initially, the alloy was formed by aluminum, copper and silicon commercially pure, fused in a clay-graphite crucible with an electric muffle furnace. After melting the mixture was poured into stainless steel AISI 304 chill and solidified under upward unsteady state heat flow conditions. Heat was directionally extracted only through a water-cooled bottom made of steel (SAE 1020). The experimental results include solidification thermal parameters such as volume fraction of the eutectic mixture, primary dendritic arm spacing and hardness.It is found that the hardness decreases with the increase of the primary dendritic spacing and with the decrease of the eutectic mixture fraction.

    Como referenciar este item
    Icon

  • IPEN-DOC 23377

    FUJITA, ISAC K.; FABBRO, INACIO M. dall; GAZZOLA, JONATHAN; SILVA, GABRIELA K. e; SANTOS, GIVANILDO A. dos; NAKAMOTO, FRANCISCO Y.; COUTO, ANTONIO A. . Experimental application using shadow moiré technique in tensile test. In: BRAZILIAN MRS MEETING, 15th, September 25-29, 2016, Campinas, SP. Abstract... São Carlos, SP: Aptor Software, 2016. p. 1041-1041.

    Abstract: Non-destructive testing can determine the occurrence of failures individually material and among them are the optical methods that use optical interferometry and produce fringes to determine strain and stress rates of an object. The moiré techniques are based on the moiré phenomenology and characterized to be an effect resulting from the geometrical interference between two or more overlapping grids, generating patterns of lucid and dark lines which are denoted by moiré fringe patterns. The shadow moiré technique consists in designing a grid ahead of the object that serves as a reference grid. The shadow of the projected grid on the object generates a second grid, in this case works as a grid object and interacting with the reference grid to the formation of fringes. The experiment was consisted of submitting a standardized test piece to a strain test in universal testing machine and verify, through the shadow moiré technique, the behavior of the specimen surface. The different coloring in the treatment of the images, because it is a tensile test, can be associated with the distribution of stress and deformation along the specimen. Indeed, where there is greater concentration of tension is where the breakdown occurs, therefore it is suggested that the shadow moiré techniques in tensile test showed the region of greatest tension and subject to breakdown. The studies of plots showed the existence of relationship between the number of fringes and the information about the material. To explore this result would be necessary to capture the image at the time of a test and check the displacement of the fringes and, consequently, the distribution of stress and strain field. The continuity of this work may add innovations in the analysis of stresses and strains materials, thus contributing to other areas to take ownership of this methodology and use these methods to the development of knowledge and science.

    Como referenciar este item
    Icon

  • IPEN-DOC 23394

    RIBEIRO, ALEXANDRE N.; KALLAS, CLAUDETE; SANTOS, GIVANILDO A. dos; NAKAMOTO, FRANCISCO Y.; MORO, JOAO R.; COUTO, ANTONIO A. ; MELO, HERCILIO G. de. The effect of the microstructure upon corrosion resistance of an Al-10wt% Si-2wt%Cu alloy. In: BRAZILIAN MRS MEETING, 15th, September 25-29, 2016, Campinas, SP. Abstract... São Carlos, SP: Aptor Software, 2016. p. 1062-1062.

    Abstract: In general, the corrosion behavior strongly depends on the structural morphology and chemical composition. The literature shows relationships between the corrosion behavior and the structural morphology of the secondary dendrite spacing [1]. The objective of this study is to investigate the influence of the microstructure of an Al-10wt%Si-2wt%Cu alloy in its corrosion resistance. In this work, an Al-10wt%Si-2wt%Cu alloy was solidified under upward unsteady state heat flow conditions. Heat was directionally extracted only through a watercooled bottom made of steel (SAE 1020). The aim of the present work is to investigate the influence of the microstructure of this alloy upon corrosion resistance. Experimental results include primary dendrite arm spacings (l1) and capacitances values (ZC P E ). The corrosion behavior was analysed by electrochemical impedance spectroscopy technique conducted in a 3% NaCl solution at room temperature. Coarser dendritic structures tend to improve the corrosion resistance of an Al-10wt%Si-2wt%Cu alloy.

    Como referenciar este item
    Icon

  • IPEN-DOC 23395

    RIBEIRO, ALEXANDRE N.; SANTOS, GIVANILDO A. dos; NAKAMOTO, FRANCISCO Y.; KALLAS, CLAUDETE; COUTO, ANTONIO A. ; MELO, HERCILIO G. de; HERNANDEZ, ROCIO D.P.B.. The influence of the microstructure upon corrosion resistance of an Al-10wt% Si-5wt%Cu alloy. In: BRAZILIAN MRS MEETING, 15th, September 25-29, 2016, Campinas, SP. Abstract... São Carlos, SP: Aptor Software, 2016. p. 1060-1061.

    Abstract: The need of the industries achieves better specific properties of materials, make to develop studies to meet this demand. For the automotive industry the most interesting properties are low specific weight, low coefficient of thermal expansion, wear resistance at high temperatures and high corrosion resistance. In this context, new materials have been considered, in particular AlSiCu alloys. [1, 2]. In general, the corrosion behavior strongly depends on the structural morphology and chemical composition [3]. In this work, an Al-10wt%Si-5wt%Cu alloy was solidified under upward unsteady state heat flow conditions. Heat was directionally extracted only through a water-cooled bottom made of steel (SAE 1020). The aim of the present work is to investigate the influence of the microstructure of this alloy upon corrosion resistance. Experimental results include primary dendrite arm spacing (l1) and capacitances values (ZCPE). The corrosion behavior was analysed by electrochemical impedance spectroscopy technique conducted in a 3% NaCl solution at room temperature. Coarser dendritic structures tend to improve the corrosion resistance of an Al-10wt%Si-5wt%Cu alloy.

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.