  • IPEN-DOC 26803

    SAEKI, MARGARIDA J.; GARCIA, JOÃO I.M.M.; FERNANDES, CELIO J.C.; ROSSI, MARIANA C.; SILVA, WILLIAM de M.; MARTINEZ, LUIS G. ; ZAMBUZZI, WILLIAN F.. Characterization of titanium surface modified by calcium titanate. In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 28th, August 18-23, 2019, Cancun, México. Abstract... Ciudad de México, México: Sociedad Mexicana de Materiales, 2019.

    Abstract: Coatings based on apatite and others that contain calcium play an important role for the osseointegration with the implant. It is believed that released calcium induces a specific biological response to the living tissue establishing a stable chemical bonding between formed bone and implants. The mechanical anchorage of implants also depends on the surface structure and morphology. In this work, the titanium surface was modified by calcium titanate, which was deposited by sol-gel method combined to the dip coating technique followed by heat treatments. Two different emersion rate (5 and 10 cm/min) were used as well as the number of coatings were varied. The temperature of this treatment was established based on the results of the thermal analysis (TG/DTA). The surfaces were characterized by X-ray diffractometry (DRX), Scanning Electron Microscopy (SEM) and water contact angle measurement. The corrosion behavior of modified surfaces was evaluated by electrochemical method (polarization curves) in balanced saline Hanks solution. Finally, biological test was carried out by the analysis of cellular viability and adhesion of MC3T3-E1 (subclone 4), mouse pre-osteoblastic cells (ATCC CRL-2593), using MTT and crystal violet assays, respectively, after 24h incubation at 37oC in 5% CO2 atmosphere. The coating consists of anatase TiO2 (PDF 21-1272) and calcium titanate (CaTiO3, PDF 43-226). SEM analysis showed that homogeneous films with 0.8μm of thickness are provided when they are prepared by only one immersion and that the films increase the resistence to corrosion. The coating increases the wettability as the water contact angle decreases from 90o±10o for cp Ti (low interstitial titanium) to 34 o±5o. The biological test shows that the modifications do not interfere on the osteoblast viability and adhesion, however, the morphological analysis of preosteoblasts cultured on the modified Ti-surface by SEM shows that the coatings promote a cell spreading.

    Como referenciar este item
    Icon

  • IPEN-DOC 18451

    SILVA, SUELANNY C. da; SAEKI, MARGARIDA J.; KANENO, RAMON; FARIA JUNIOR, RUBENS N.; TAKIISHI, HIDETOSHI . Estudo de citoxicidade em nanoparticulas de Pr-Fe-B para aplicação em hipertermia. In: CONGRESSO BRASILEIRO DE ENGENHARIA E CIENCIA DOS MATERIAIS, 20., 4-8 de novembro, 2012, Joinville, SC. Resumos... 2012. p. 8237.

    Palavras-Chave: permanent magnets; hydrogen; praseodymium alloys; iron alloys; boron alloys; hydrogenation; heat treatments

    Como referenciar este item
    Icon

  • IPEN-DOC 21610

    SILVA, I.V. da; YOSHITO, W.K. ; MARTINS, M.L.; ICHIKAWA, R.U. ; SANTOS, D.I. dos; MARTINEZ, L.G. ; CENTENO, M.A.; ODRIOZOLA, J.A.G.; SAEKI, MARGARIDA J.. Influence of Ph on the densification of BaZrsub(0.1)Cesub(0.7)Ysub(0.1)Ybsub(0.1)Osub(3-'gamma'). In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 24th, August 16-20, 2015, Cancun, Mexico. Abstract... 2015.

    Palavras-Chave: ph value; synthesis; doped materials; zirconates; barium compounds; cerium compounds; yttrium compounds; ytterbium compounds

    Como referenciar este item
    Icon

  • IPEN-DOC 26804

    ROSSI, MARIANA C.; BAYERLEIN, DANIEL L.; KRIECK, ANDRE M.T.; BRANDÃO, JAQUELINE de S.; PFEIFER, JOÃO P.H.; ROSA, GUSTAVO dos S.; STIEVANI, FERNANDA de C.; MARTINEZ, LUIS G. ; SAEKI, MARGARIDA J.; ALVES, ANA L.G.. Influence of space holder on the biocompatibility of Ti-34Nb-6Sn alloy prepared by powder metallurgy. In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 28th, August 18-23, 2019, Cancun, México. Abstract... Ciudad de México, México: Sociedad Mexicana de Materiales, 2019.

    Abstract: Development of metallic materials for denistry and orthoapedic area have been increasing, due to in world life expectancy and the significantly numbers of accide nts. Due to problems of failure in available commercial materials implantation, as well as the discomfort of patient because the high elastic modulus, these devices need to be improved or news implants should be sought. This study was intended to develop a porous alloy, Ti-34-Nb-6Sn/Mg wich can help the ingrowth bone tissue when implanted, by the powder metallurgy. After the milling powders in the high energy mill, were compacted and sintered. Both, powders and sintered materials were chacarterized by X-ray Difraction (XRD), Scanning Electron Microscopy (SEM) and semi-quantitative compositional analysis (EDS). The apparent porosity was measured through the Arquimed’s Method. The toxicity this material was evaluated by MTT assay, using the equine mesenchemal stem cells derivated of bone marrow (bmMSC) according to ISO 109935. The bmMSCs morphological analysis in contact on the material surface using SEM. The Mg evaporation was confirmed by EDS and XRD after sintering. The XRD indicate there is predominantly beta phase than alpha. The apparent porosity was higher in alloy with Mg space holder. The materials do not presented particular cytotoxic in direct and indirect contact. Metallurgic powder tecnhique promoted effectively macropores formation in Ti-34Nb-6Sn/Mg alloy, wich possibly further bmMSCs adhesion.

    Como referenciar este item
    Icon

  • IPEN-DOC 21609

    PARRA, JOAO P.R.L.L.; MARTINS, MURILLO L.; MORETTO, GUSTAVO M.; ICHIKAWA, RODRIGO ; MARTINEZ, LUIZ G. ; COLAUTO, FABIANO; ORTIZ, WILSON A.; MIRANDA, JOSE R. de A.; ZAMBUZZI, WILLIAN F.; SAEKI, MARGARIDA J.. Influence of Synthesis variable on the structure and magnetic response of Mnsub(0.74)Znsub(0.25)Fesub(2.8)Osub(4). In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 24th, August 16-20, 2015, Cancun, Mexico. Abstract... 2015.

    Palavras-Chave: manganese compounds; zinc compounds; ferrites; synthesis; nanoparticles; toxicity; magnetic properties; coprecipitation

    Como referenciar este item
    Icon

  • IPEN-DOC 30156

    GARCIA, JOAO I.M.M.; GOMES, ANDERSON M.; ZAMBUZZI, WILLIAN F.; ICHIKAWA, RODRIGO U. ; SAEKI, MARGARIDA J.. Influence of temperature on obtaining apatites by sol- gel method. In: BRAZIL MRS MEETING, 21st, October 1-5, 2023, Maceió, AL. Abstract... São Carlos, SP: Aptor Software, 2023. p. 434-434.

    Abstract: Calcium phosphate-based ceramics (apatites) are synthetic materials that have a chemical composition similar to bone tissue, which makes them interesting to use as biomaterials [1]. In this work, the apatite precursor sols at concentrations of 0.7 mol/L and 1.4 mol/L are prepared by dissolving calcium nitrate and phosphorus pentoxide in ethanol. The sols are kept at rest for 24 hours for hydrolysis (gelatinization) under room temperature and humidity. After hydrolysis, the resulting gels are dried at 80°C to remove the organic solvent and then calcined under different temperatures (from 500°C to 1200°C, with increments of 100°C) for 8h [2]. The X-ray diffraction analysis of the samples by the Rietveld method indicates that the samples are composed of monoclinic and hexagonal hydroxyapatite (HAp), the former being predominant, and calcium β-triphosphate (TCP)[3] . For the material started from the sol with a concentration of 0.7 mol/L, the hydroxyapatite fraction increases from 28.8% to 66.5% when the calcination temperature increases from 500°C to 800°C. Above this temperature, the fraction of this phase decreases. With a concentration of 1.4 mol/L, the hydroxyapatite fraction decreases from 88.2% to 19.5% progressively with increasing temperature from 500°C to 1200°C. The micrographs revealed the formation of particulate but porous materials that agglomerate without sintering up to a temperature of 900°C, from where the formation of sintered and dense agglomerates is observed. The results of the EDX analysis showed a Ca/P molar ratio of around 1.5 for all materials. The cytotoxicity assay, using pre-osteoblast cells (MC3T3-E1, Subclone 4) by non-direct contact of 24h, showed that cell viability and adhesion did not differ from those of the control. A decrease in viability and adhesion was observed for samples prepared at a concentration of 0.7 mol/L and calcined at temperatures above 900°C.

    Como referenciar este item
    Icon

  • IPEN-DOC 26837

    ROSSI, MARIANA C.; BAYERLEIN, DANIEL L. ; BRANDÃO, JAQUELINE de S.; PFEIFER, JOÃO P.H.; ROSA, GUSTAVO dos S.; KRIECK, ANDRE M.T.; MARTINEZ, LUIS G. ; SAEKI, MARGARIDA J.; ALVES, ANA L.G.. Preparation of porous ternary alloy Ti-34-Nb-6Sn / Mg for the implant. In: BRAZIL MRS MEETING, 18th, September 22-26, 2019, Balneário Camburiú, SC. Abstract... São Carlos, SP: Aptor Software, 2019. p. 1042-1042.

    Abstract: Titanium alloys are designed in order to provide attractive mechanical properties, including Young's modulus, high mechanical strength and biocompatibility [1]. These properties are achieved when titanium structured under β phase, and the selection of non-toxic beta-stabilizing metals is important for the improvement of the alloys. In order to create a good interaction at the bone-implant interface, it is interesting that these biomaterials also have adequate porosities for the bone cells to adhere on its surface, and the bone tissue to grow around the prosthesis. Thus, the purpose of this work was to produce the Ti-34-Nb-6Sn alloy by the powder metallurgy technique allied to the magnesium space holder. After the synthesis, the structure of the material was characterized by X-ray diffractometry (XRD) and its morphological and compositional analysis, carried out by Scanning Electron Microscopy (SEM) and X-ray dispersive energy (EDX). The apparent porosity analysis was made by the Archimedes method. In the biological assay, stem cells derived from equine bone marrow were seeded on the surface of the materials in order to obtain information about cytotoxicity and cell adhesion. The results of XRD and MEV confirmed the formation of the alloy (PDF: 25-977), being that the proportion of phase β was greater than the phase α (PDF: 44-1288,41-1352), and the evaporation of Mg, as well as a significant increase of porosity, which was also confirmed by the Archimedes method. Additionally, according to SEM, the cells showed good adhesion on the surface of the material, as well as inside the formed pores. According to the techniques used, it was then possible to obtain β phase rich titanium alloy with significant porosity on which the cells adhered satisfactorily.

    Como referenciar este item
    Icon

  • IPEN-DOC 19864

    MARTIN, JUAN G.; YOSHITO, WALTER K. ; DUVAIZEN, JOSE H.; TAKIISHI, HIDETOSHI ; SAEKI, MARGARIDA J.. Surface modification of the Ti6AL4V alloy for biomedical application. In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 22th, August 11, 2013, Cancum, Mexico. Abstract... 2013. p. 80.

    Palavras-Chave: biological materials; titanium alloys; titanium oxides; apatites; sol-gel process; surface coating

    Como referenciar este item
    Icon

  • IPEN-DOC 26972

    MOURA, TIAGO F.A.; NAVARRO, RAPHAELLA; SHIOTSUKI, AUGUSTO K.; UTIYAMA, ANA P.M.S.; ICHIKAWA, RODRIGO U. ; MATOS, RONALDO V.R.; CASTRO, GUSTAVO R.; YOSHITO, WALTER K. ; MARTINEZ, L.G. ; MIRANDA, JOSE R.A.; SAEKI, MARGARIDA J.. The influence of iron content and alkaline concentration on Mn0.75Zn0.25FeyO4 structure, surface charge and acb response. In: BRAZIL MRS MEETING, 16th, September 10-14, 2017, Gramado, RS. Abstract... São Carlos, SP: Aptor Software, 2017. p. 578-578.

    Abstract: Nanotechnology applied on magnetic material provide a good opportunity to develop biomaterials as tracers for Alternating Current Biosuceptometry (ACB)and Magnetic Resonance Imaging (MRI) to diagnose certain diseases as cancer. The magnetic nanoparticles can still constitute drug carrier systems and hyperthermia agent for cancer treatment. Neverthless, the efficiency for therapy and diagnosis depends on the magnetic susceptibility. In this work, the ferrite nanoparticles with nominal composition Mn0.75Zn0.25FeyO4, where 1.5 ≤ y ≤ 2.8, were synthesized by the co-precipitation method and, the influence of iron content and concentration of precipitating agent on the structure, ACB response and surface charge was analyzed. It was noted that the synthesis using alkaline metal hydroxide between 0.1, 0.15 and 0.2 mol/L provides single-phase materials [ICSD 28515 (PDF - 742 402), space group Fd3m]. The higher concentration (0.25 mol/L) leads to materials with higher crystallinity and similar ACB response to those precipitated by lower concentration base, despite the secondary phase. A surface charge of 30 mV in module was achieved, which decreased as the concentration of the precipitating agent increased.

    Como referenciar este item
    Icon

  • IPEN-DOC 23846

    NAVARRO, RAPHAELLA; MOURA, TIAGO F.A.; YOSHITO, WALTER K. ; ICHIKAWA, RODRIGO ; MARTINEZ, LUIZ G. ; MATOS, RONALDO V.R.; MIRANDA, JOSE R. de A.; SAEKI, MARGARIDA J.. The influence of synthesis parameters on the structure and acb response of Mn0.75 Zn0.25FeyO4 ferrite. In: INTERNATIONAL MATERIALS RESEARCH CONGRESS, 25th, August 14-19, 2016, Cancún, Mexico. Abstract... 2016.

    Abstract: The interest to use magnetic nanoparticles in biomedicine has increased due to their inducible magnetic properties[1-4]. In the treatment of certain diseases as cancer, it has been used to constitute drug carrier systems[2,3] as well as hyperthermia agents[3,4]. These materials can also be used as a tracer in the diagnosis by Magnetic Resonance Imaging (MRI)[3,4] and Alternating Current Biosuceptometry (ACB)5, which are techniques that do not use ionizing radiation. Neverthless, the sensitivity of these techniques depend on the magnetic susceptibility of tracers. In this work, the ferrite nanoparticles with the composition of Mn0.75Zn0.25FeyO4 (ferrite), where 1.5 ? y ? 2.8, were synthesized by the co-precipitation method and the influence of iron content, reaction time and concentration of precipitating agent on the structure and ACB response was analyzed. It was noted that the synthesis using alkaline metal hydroxide between 0.1 and 0.2 mol/L provides single-phase materials with spinel structure [ICSD 28515 (PDF - 742 402), space group Fd3m]. The higher concentration (0.2 mol/L) leads to materials with higher crystallinity and adequate performance for the ACB technique. The longer the reaction time the greater is the magnetic susceptibility for compositions wherein the iron is in excess (y>2.0). Also, the susceptibility is higher for ferrites with excess of iron.

    Como referenciar este item
    Icon

  • IPEN-DOC 22305

    PARRA, JOAO P.R.L.L.; MARTINS, MURILLO L.; MORETTO, GUSTAVO M.; ICHIKAWA, RODRIGO ; MARTINEZ, LUIZ G. ; CORAUTO, FABIANO; MIRANDA, JOSE R.A.; SAEKI, MARGARIDA J.. Traçadores magnéticos Mnsub(0.74)Znsub(0.25)Fesub(2.8)Osub(4) para diagnóstico por BAC: influência da variável de síntese na estrutura e resposta magnética / Synthesis of magnetic tracers Mnsub(0.74)Znsub(0.25)Fesub(2.8)Osub(4) for the diagnosis by ACB: influence of synthesis variable on the structure and magnetic response. In: CONGRESSO DE FISICA APLICADA À MEDICINA, 10., 24-27 de setembro, 2014, Botucatu, SP. Resumo... 2014.

    Palavras-Chave: tracer techniques; nanoparticles; ferrites; diagnostic techniques; ph value; precipitation; synthesis; magnetic properties

    Como referenciar este item
    Icon

A pesquisa no RD utiliza os recursos de busca da maioria das bases de dados. No entanto algumas dicas podem auxiliar para obter um resultado mais pertinente.

✔ É possível efetuar a busca de um autor ou um termo em todo o RD, por meio do Buscar no Repositório , isto é, o termo solicitado será localizado em qualquer campo do RD. No entanto esse tipo de pesquisa não é recomendada a não ser que se deseje um resultado amplo e generalizado.

✔ A pesquisa apresentará melhor resultado selecionando um dos filtros disponíveis em Navegar

✔ Os filtros disponíveis em Navegar tais como: Coleções, Ano de publicação, Títulos, Assuntos, Autores, Revista, Tipo de publicação são autoexplicativos. O filtro, Autores IPEN apresenta uma relação com os autores vinculados ao IPEN; o ID Autor IPEN diz respeito ao número único de identificação de cada autor constante no RD e sob o qual estão agrupados todos os seus trabalhos independente das variáveis do seu nome; Tipo de acesso diz respeito à acessibilidade do documento, isto é , sujeito as leis de direitos autorais, ID RT apresenta a relação dos relatórios técnicos, restritos para consulta das comunidades indicadas.

A opção Busca avançada utiliza os conectores da lógica boleana, é o melhor recurso para combinar chaves de busca e obter documentos relevantes à sua pesquisa, utilize os filtros apresentados na caixa de seleção para refinar o resultado de busca. Pode-se adicionar vários filtros a uma mesma busca.

Exemplo:

Buscar os artigos apresentados em um evento internacional de 2015, sobre loss of coolant, do autor Maprelian.

Autor: Maprelian

Título: loss of coolant

Tipo de publicação: Texto completo de evento

Ano de publicação: 2015

✔ Para indexação dos documentos é utilizado o Thesaurus do INIS, especializado na área nuclear e utilizado em todos os países membros da International Atomic Energy Agency – IAEA , por esse motivo, utilize os termos de busca de assunto em inglês; isto não exclui a busca livre por palavras, apenas o resultado pode não ser tão relevante ou pertinente.

✔ 95% do RD apresenta o texto completo do documento com livre acesso, para aqueles que apresentam o significa que e o documento está sujeito as leis de direitos autorais, solicita-se nesses casos contatar a Biblioteca do IPEN, bibl@ipen.br .

✔ Ao efetuar a busca por um autor o RD apresentará uma relação de todos os trabalhos depositados no RD. No lado direito da tela são apresentados os coautores com o número de trabalhos produzidos em conjunto bem como os assuntos abordados e os respectivos anos de publicação agrupados.

✔ O RD disponibiliza um quadro estatístico de produtividade, onde é possível visualizar o número dos trabalhos agrupados por tipo de coleção, a medida que estão sendo depositados no RD.

✔ Na página inicial nas referências são sinalizados todos os autores IPEN, ao clicar nesse símbolo será aberta uma nova página correspondente à aquele autor – trata-se da página do pesquisador.

✔ Na página do pesquisador, é possível verificar, as variações do nome, a relação de todos os trabalhos com texto completo bem como um quadro resumo numérico; há links para o Currículo Lattes e o Google Acadêmico ( quando esse for informado).

ATENÇÃO!

ESTE TEXTO "AJUDA" ESTÁ SUJEITO A ATUALIZAÇÕES CONSTANTES, A MEDIDA QUE NOVAS FUNCIONALIDADES E RECURSOS DE BUSCA FOREM SENDO DESENVOLVIDOS PELAS EQUIPES DA BIBLIOTECA E DA INFORMÁTICA.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

1. Portaria IPEN-CNEN/SP nº 387, que estabeleceu os princípios que nortearam a criação do RDI, clique aqui.


2. A experiência do Instituto de Pesquisas Energéticas e Nucleares (IPEN-CNEN/SP) na criação de um Repositório Digital Institucional – RDI, clique aqui.

O Repositório Digital do IPEN é um equipamento institucional de acesso aberto, criado com o objetivo de reunir, preservar, disponibilizar e conferir maior visibilidade à Produção Científica publicada pelo Instituto, desde sua criação em 1956.

Operando, inicialmente como uma base de dados referencial o Repositório foi disponibilizado na atual plataforma, em junho de 2015. No Repositório está disponível o acesso ao conteúdo digital de artigos de periódicos, eventos, nacionais e internacionais, livros, capítulos, dissertações, teses e relatórios técnicos.

A elaboração do projeto do RI do IPEN foi iniciado em novembro de 2013, colocado em operação interna em julho de 2014 e disponibilizado na Internet em junho de 2015. Utiliza o software livre Dspace, desenvolvido pelo Massachusetts Institute of Technology (MIT). Para descrição dos metadados adota o padrão Dublin Core. É compatível com o Protocolo de Arquivos Abertos (OAI) permitindo interoperabilidade com repositórios de âmbito nacional e internacional.

O gerenciamento do Repositório está a cargo da Biblioteca do IPEN. Constam neste RI, até o presente momento 20.950 itens que tanto podem ser artigos de periódicos ou de eventos nacionais e internacionais, dissertações e teses, livros, capítulo de livros e relatórios técnicos. Para participar do RI-IPEN é necessário que pelo menos um dos autores tenha vínculo acadêmico ou funcional com o Instituto. Nesta primeira etapa de funcionamento do RI, a coleta das publicações é realizada periodicamente pela equipe da Biblioteca do IPEN, extraindo os dados das bases internacionais tais como a Web of Science, Scopus, INIS, SciElo além de verificar o Currículo Lattes. O RI-IPEN apresenta também um aspecto inovador no seu funcionamento. Por meio de metadados específicos ele está vinculado ao sistema de gerenciamento das atividades do Plano Diretor anual do IPEN (SIGEPI). Com o objetivo de fornecer dados numéricos para a elaboração dos indicadores da Produção Cientifica Institucional, disponibiliza uma tabela estatística registrando em tempo real a inserção de novos itens. Foi criado um metadado que contém um número único para cada integrante da comunidade científica do IPEN. Esse metadado se transformou em um filtro que ao ser acionado apresenta todos os trabalhos de um determinado autor independente das variáveis na forma de citação do seu nome.